LEVL Coat 271 — finishing layer for methyl methacrylate floors
LEVL (INGRI)

LEVL Coat 271 — finishing layer for methyl methacrylate floors

Methyl methacrylate floors

The MMA system is completed by the LEVL Coat 271 finishing layer, applied over the LEVL Coat 573 main layer with a flat trowel and back-rolling, or simply by roller. The carboacrylate resin cures quickly: at +20 °C the floor can be walked on after about 4 hours, and with LEVL Coat 075 accelerator work is carried out even at −10 °C. Taber abrasion is up to 45 mg, adhesion of the whole system at least 2.5 MPa; the coating resists aggressive chemicals, water and UV. It is used in warehouses, workshops, car parks, food and wet rooms, and on open areas.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typemethyl methacrylate (MMA) floors
Usewarehouses and logistics, production workshops, car parks and ramps, retail and public buildings, wet rooms, food and pharmaceutical, chemically resistant, decorative, outdoor areas
Basecolourless carboacrylate (MMA) resin; LEVL Coat 070 catalyst, at sub-zero temperatures LEVL Coat 075 accelerator
Colourmatches the colour of the filler in the main layer; tinting with dry mineral pigment
Packaging1 kg metal can; 10 and 20 kg metal pails; 200 kg steel drums; LEVL Coat 070 catalyst depending on temperature: −10 °C 4 % (+ accelerator 2 %), 0 °C 3 % (+2 %), +10 °C 2.5 % (+1 %), +20 °C 2 %, +30 °C 1 % (by weight)
Application methodfinishing layer of highly filled carboacrylate systems with coloured wear-resistant filler (over LEVL Coat 573), indoor and outdoor work: with a flat trowel and back-rolling, or by roller
Application temperatureair and substrate from −10 °C to +30 °C; material +5…+30 °C (optimum +17…+23 °C); air humidity no more than 80 %; substrate moisture no more than 5.0 % by weight; 3 °C above the dew point; below 0 °C, with LEVL Coat 075 accelerator; supply and exhaust ventilation required
Curingfoot traffic: −10 °C ~24 h, 0 °C ~12 h, +10 °C ~6 h, +20 °C ~4 h, +30 °C ~2 h; light loads: ~48 / ~48 / ~12 / ~12 / ~6 h; full strength gain: ~4 / ~3 / ~2 / ~1 days / ~12 h; pot life ~13–25 min, curing ~30–60 min
Key propertiesTaber abrasion (CS10/1000 g/1000 rev.) no more than 45 mg; ultimate tensile strength at least 10 MPa; relative elongation at least 0.9 %; Shore D hardness (7 days) at least 45; adhesion in the 171/573/271 system at least 2.5 MPa; density 0.95 ± 0.05 g/cm³; non-volatile content at least 98 %; high resistance to aggressive chemicals, water, UV and bacteriological attack; service temperature from −30 °C to +60 °C, short-term up to +90 °C
Layer thickness0.4–1.0 mm
Consumption0.4–1.0 kg/m²; in systems: finish over a textured layer 0.7 kg/m² (+ LEVL Coat 070 0.014 kg/m²), over a smooth-textured layer 1.00 kg/m²
Shelf life12 months when stored at 0 °C to +25 °C; 6 months when stored above +25 °C
StandardsTU 2257-038-94613022-15; test methods GOST 31992.1, GOST 11262, GOST 24621, GOST 31939, GOST 28574

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.