Epolast — solvent-free epoxy self-levelling floor

Epoxy floors

Epolast is poured in a single layer over Epoksol-2MS epoxy primer and spread with a notched trowel or squeegee, followed by rolling with a spiked roller. The compound is odourless, retains high chemical and abrasion resistance even at elevated humidity and withstands water, petrol, 40 % NaOH, 10 % sulphuric and 37 % hydrochloric acid for at least 72 h. It can be laid on concrete as well as on rigid metal and timber structures; service properties develop within 10 days.

Specifications

ManufacturerKRASKO — OOO “NPO KRASKO”, Moscow Region
Typeepoxy floors
Useproduction halls, warehouses and logistics, food and pharmaceutical, chemically resistant, wet rooms, retail and public, decorative
BaseTwo-component solvent-free epoxy compound; base — epoxy resin
ColourSemi-gloss (gloss at 60° at least 36 GU); RAL 7040; tinting to RAL Classic, NCS Index, Symphony to order from 300 kg
Packaging30 kg and by agreement with the customer
Application methodFinish coat over Epoksol-2MS epoxy primer (concrete at least M250); preparation to SP 29.13330.2011 and SP 71.13330.2017: cleaning, filling, drying (per the description — to moisture not more than 15 %), grinding to remove laitance. Pour onto a dry clean surface, spread with a notched trowel/squeegee, roll with a spiked roller; in one layer; relative humidity not more than 80 %; pot life at least 1 h. Can be laid on concrete, rigid metal and timber structures.
Application temperaturefrom +10 °C to +30 °C
CuringDrying to degree 3 at (20±2) °C — not more than 24 h; service properties at 20 °C — after 10 days
Key propertiesNon-volatile content by weight comp. A 95–100 %; density of comp. A 1.7–1.9 g/cm³; Brookfield viscosity 5000–10000 mPa·s; pendulum hardness at least 0.50; gloss at 60° at least 36 GU; hiding power not more than 500 µm; resistance for at least 72 h to water, petrol, 40 % NaOH, 10 % sulphuric and 37 % hydrochloric acid; service temperature from −50 °C to +80 °C
Layer thickness1–3 mm in one layer
Consumption2–5.5 kg/m² (at a thickness of 1–3 mm)
Shelf life6 months from the date of manufacture; storage from −40 °C to +40 °C
StandardsTU 20.30.12-004-01524656-2017; preparation to SP 29.13330.2011 and SP 71.13330.2017

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.