BIRSS 59 S1 M600 Moroz — flowable R4 mix for repairing pavements in frost
BIRSS

BIRSS 59 S1 M600 Moroz — flowable R4 mix for repairing pavements in frost

Flowable repair mortars

BIRSS 59 S1 M600 Moroz, a non-shrink plastic mix for structural repair of horizontal concrete and reinforced concrete structures, is placed at temperatures from −15 to +5 °C. It is used to restore road pavements and runways, bridges, car parks, industrial floors and equipment foundations. If the mortar hardens at −15 °C, at 28 days it reaches 30 MPa in compression, at +20 °C 60 MPa; class R4, water impermeability W14, frost resistance F2 400.

Specifications

ManufacturerBIRSS — AO Opytny Zavod Sukhikh Smesey (Experimental Dry Mix Plant), Moscow
Typeflowable repair mortars
Useroads and airfields, bridges and overpasses, floors, equipment foundations, hydraulic structures and dams
BaseBIRSS 59 S1 M600 Moroz rapid-hardening dry repair mix is a material based on special cements, high-quality natural fillers and chemical admixtures. When mixed with water it forms a non-shrink, plastic, non-segregating mortar with high water retention and excellent…
Colourlight grey
Packagingbags 25 / 40 kg
Application methodFor structural repair of horizontal concrete and reinforced concrete structures: repair of road pavements and airfield runways, bridge spans and bridge decks, concrete pavements of parking areas in all climatic zones; repair of industrial floors, walls and equipment foundations indoors and in open areas subject to heavy mechanical loads and aggressive media (mineral oils, lubricants, etc.); repair of concrete and reinforced…
Application temperature−15…+5 °C
Key propertiesmaximum aggregate size, mm: 5.0; workability grade: Rk4/ 18-22; setting time: initial not earlier than 30 min, final not later than 60 min; workability retention, min: 30; bond strength to substrate, MPa: 2.5; compressive strength, MPa, not less than; 1 day (at t=20 °C/ at t=-15 °C); 3 days (at t=20 °C/ at t=-15 °C); 7 days (at t=20 °C/ at t=-15 °C); 28 days (at t=20 °C/ at t=-15 °C) 20/5 30/10 45/15 60/30; flexural strength, MPa, not less than; 28 days (at t=20 °C/ at t=-15 °C) 8/5; modulus of elasticity, MPa: 25,000; water impermeability: W14; frost resistance: F2 400; frost resistance of the contact zone: 100; sulphate resistance coefficient: 0.9; service temperature, °C: from -50 to +70
Standardsclass R4 to GOST R 56378; STO 05668056-004-2012

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.