Epoksipol-2 — epoxy self-levelling floor for damp concrete
KRASKO

Epoksipol-2 — epoxy self-levelling floor for damp concrete

Epoxy floors

The main distinction of Epoksipol-2 is that it works on damp substrates: it may be applied to fresh concrete with residual moisture up to 15 % and to floors without waterproofing. On dry concrete it is laid over Epoksol-2MS primer, on damp and old concrete over Epoksol water-epoxy impregnation. The coating forms a moisture barrier, protects against mould and fungus and withstands water, petrol, alkalis and acids for at least 72 h.

Specifications

ManufacturerKRASKO — OOO “NPO KRASKO”, Moscow Region
Typeepoxy floors
Useproduction halls, warehouses and logistics, food and pharmaceutical, chemically resistant, wet rooms, retail and public
BaseTwo-component self-levelling compound based on modified epoxy resin, free of organic solvents
ColourSemi-matt texture (gloss at 60° 36–80 GU); grey
Packaging25 kg and by agreement with the customer
Application methodOn a dry concrete substrate — over Epoksol-2MS epoxy primer; on a damp (up to 15 %) and old substrate — over Epoksol water-epoxy primer-impregnation. Application on damp and fresh concrete (residual moisture up to 15 %) and on floors without waterproofing is permitted. Preparation to SP 29.13330.2011 and SP 71.13330.2017; spread with a notched trowel/squeegee, roll with a spiked roller; relative humidity not more than 90 %
Application temperaturefrom +10 °C to +30 °C
CuringDrying to degree 3 at (20±2) °C — not more than 24 h; service properties at 20 °C — after 10 days
Key propertiesNon-volatile content by weight comp. A 95–99 %; density of comp. A 1.85±0.05 g/cm³; Brookfield viscosity 5000–9000 mPa·s; pendulum hardness at least 0.50; gloss at 60° 36–80 GU; hiding power not more than 400 µm; sag-free film thickness at least 50 µm; resistance for at least 72 h to water, petrol, 40 % NaOH, 10 % sulphuric and 37 % hydrochloric acid; service temperature from −50 °C to +80 °C
Layer thickness1–3 mm (levelling layer)
Shelf life6 months from the date of manufacture; storage from −40 °C to +40 °C
StandardsTU 20.30.12-004-01524656-2017; state registration certificate; preparation to SP 29.13330.2011 and SP 71.13330.2017

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.