Wetisol S-MP3 — primer for polyurea on PVC and metal
Wetisol (INGRI)

Wetisol S-MP3 — primer for polyurea on PVC and metal

Other waterproofing materials

Wetisol S-MP3 is a one-component polyurethane primer cured by air moisture, with high elasticity and adhesion to PVC. It is used to prepare metal, tiles, natural stone, bituminous roofs, asphalt concrete, polyurethane foam and PVC roof coverings, as well as concrete, brick and stone, before polycarbamide and polyurethane coatings. Another purpose is as an intermediate coat when overcoating WETISOL LAM 361 mastic. The primer is applied at +5…+35 °C and tolerates mineral substrate moisture of up to 8%.

Specifications

ManufacturerWetisol (INGRI) — OOO “Ingri”
Typewaterproofing material
Baseone-component polyurethane-based material, cures with air moisture
Colourtransparent liquid with a yellowish tint
Packaging10 kg and 19 kg bucket; 220 kg drum
Application methodpriming before polycarbamide (and polyurethane) coatings on metal, dense mineral substrates (tiles, natural stone), non-rigid substrates (bituminous roofs, asphalt concrete, polyurethane foam), PVC roof coverings and PVC products, as well as on concrete, brick, stone; intermediate coat when overcoating WETISOL LAM 361 mastic; metal — abrasive blast cleaning to degree 2 per GOST 9.402 / Sa 2½, Rz > 60 µm, salt and pH control; tiles, stone — shot or sand blasting; PVC — washing (pressure washers permitted), drying, degreasing; by brush, velour roller (ZOGEL Z360-2241) or airless sprayer (ZOGEL ZP-1E300, ZP-4E240); pump — WETISOL S-Clean, tools — solvent 646
Application temperatureambient air and substrate +5…+35 °C (+10…+25 °C recommended); material temperature +10…+30 °C (+15…+25 °C recommended); relative air humidity 40–80%; moisture of the mineral substrate max 8 wt. %; 3 °C above the dew point
Curingdrying time to degree 3 max 8 h (GOST 19007); apply the topcoat after 6–12 h at +10 °C, 4–8 h at +20 °C, 3–5 h at +30 °C, no more than 3 h at temperatures above +35 °C
Key propertiesdensity at 23 °C 1.05±0.05 g/cm³ (GOST 31992.1); drying time to degree 3 max 8 h (GOST 19007); adhesion to concrete in the system with WETISOL Spray 400 — 2.5 MPa (GOST 28574); cross-cut adhesion max 1 point (GOST 15140); dry residue 80 wt. % (GOST 31939); high elasticity and adhesion to PVC substrates; service temperature from −60 to +60 °C (short-term up to +90 °C)
Layer thicknessdry film thickness per coat 45–60 µm; 90 µm coating
Consumptiontheoretically 150 g/m² per 90 µm; metal, bituminous and PVC substrates — 0.15 kg/m²; concrete, brick, stone — 0.25 kg/m²
Shelf life6 months from the date of manufacture in unopened undamaged original containers at +5…+25 °C
StandardsTU 2312-035-94613022-14 with amendment No. 1

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.