BIRSS 59 S1 M600 — flowable R4 mix for repairing roads, bridges and airfields
BIRSS

BIRSS 59 S1 M600 — flowable R4 mix for repairing roads, bridges and airfields

Flowable repair mortars

Horizontal concrete and reinforced concrete structures are the field of application of BIRSS 59 S1 M600: road pavements and runways, bridge spans and bridge decks, car parks, industrial floors and equipment foundations, including under exposure to mineral oils and lubricants. The non-shrink plastic mortar begins to set no earlier than 40 minutes. Class R4; compressive strength 20 MPa after one day and 60 MPa at 28 days, modulus of elasticity 25,000 MPa, W 18, F2 400.

Specifications

ManufacturerBIRSS — AO Opytny Zavod Sukhikh Smesey (Experimental Dry Mix Plant), Moscow
Typeflowable repair mortars
Useroads and airfields, bridges and overpasses, floors, equipment foundations, hydraulic structures and dams
BaseBIRSS 59 S1 M600 rapid-hardening dry repair mix is a material based on special cements, high-quality natural fillers and chemical admixtures. When mixed with water it forms a non-shrink, plastic, non-segregating mortar with high water retention and excellent work…
Colourlight grey
Packagingbags 25 / 40 kg
Application methodFor structural repair of horizontal concrete and reinforced concrete structures: repair of road pavements and airfield runways, bridge spans and bridge decks, concrete pavements of parking areas in all climatic zones; repair of industrial floors, walls and equipment foundations indoors and in open areas subject to heavy mechanical loads and aggressive media (mineral oils, lubricants, etc.); repair of concrete and reinforced…
Application temperature+5…+35 °C
Key propertiesmaximum aggregate size, mm: 5.0; workability grade: Rk4/ 18-22; setting time: initial not earlier than 40 min, final not later than 60 min; workability retention, min: 30; bond strength to substrate, MPa: 2.5; compressive strength, MPa, not less than - 1 day/3 days 20/30 - 7 days/28 days 45/60; flexural strength, MPa, not less than - 1 day/3 days 5/7 - 7 days/28 days 7.5/8; modulus of elasticity, MPa: 25,000; water impermeability: W 18; frost resistance: F2 400; frost resistance of the contact zone: Fkz100; sulphate resistance coefficient: 0.9; service temperature, °C: from -50 to +70
Standardsclass R4 to GOST R 56378; STO 05668056-004-2012

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.