Elakor-PTs T2 — polyurethane-cement coating for moderate and significant loads

Polyurethane-cement floors

The second compound in the polyurethane-cement floor series is designed for moderate and significant intensity of mechanical exposure, including abrasive, impact and vibration loads, combined with heat and chemical attack. The coating is resistant to water, salt and alkali solutions, acids up to 10–20 %, oils, fats and solvents. Compressive strength is 56 MPa, Shore D hardness 80–85, continuous service temperature from −30 to +70 °C, full chemical load after 14 days.

Specifications

ManufacturerElakor — OOO “TEOKHIM-PROM”, Moscow Region
Typepolyurethane-cement floors
Useproduction workshops, warehouses and logistics, car parks and ramps, food and pharmaceutical, chemically resistant
Basepolyurethane-cement three-component self-levelling compound (self-levelling coating)
Colourgrey, light grey, beige, brown, yellow, blue, green, black; semi-matt/matt finish (the shade may change over time)
PackagingComp. “A” 3.5 kg + Comp. “B” 3.5 kg + Comp. “C” 22 kg = Kit 29 kg
Application methodSubstrate: monolithic concrete, concrete and sand-concrete screeds, grade strength not lower than M350 (B25), new concrete cured for at least 28 days; surface moisture is not limited (there must be no puddles); relative air humidity and dew point are not limited. Preparation: grinding with a terrazzo grinding machine (“000”/“00” segments) or shot blasting; anchor grooves 6-10 mm. Spread with a gauge rake with adjustable gap, roll with a spiked roller (not later than 15 min).
Application temperatureair, surface: optimum +17…+23°C; permissible +10…+30°C; material temperature +18…+22°C
Curingpot life on the surface at (20±2)°C at least 15 min; at (20±2)°C, relative air humidity 70%: foot traffic – 24 h, full mechanical load – 7 days, full chemical load – 14 days
Key propertiesA:B:C ratio by weight 3.5 : 3.5 : 22.0; density 1.92±0.02 kg/l; adhesion (GOST 28574-2014) to concrete B25 > 2.5 MPa, to concrete B40 > 4.0 MPa (failure in concrete); compressive strength (28 days) 56 MPa; flexural 20 MPa; tensile 12 MPa; Shore D hardness at least 80-85; impact strength U-2M 100 cm; Taber abrasion CS-10, 1000 g, 14 days, not more than 20 mg; service temperature -30°C…+70°C continuous, short-term for up to 2 h up to 150°C; fire hazard class KM2 (V2, D1, T1, RP1); chemical resistance: water, salt and alkali solutions of any concentration, acid solutions up to 10-20%, oils and fats of all kinds, organic solvents, petrol, diesel fuel
Layer thickness5-10 mm
Consumptiontheoretical consumption 1.92 kg per 1 m² per 1 mm of layer; allowing for filling of grooves and a 5% technological reserve – 2.05 kg
Shelf lifecomponents “A” and “B” – 12 months, component “C” – 6 months in the manufacturer's original packaging; store and transport at temperatures from +5° to +25°C
StandardsCertificate of conformity (fire safety) “Elakor-PTs”, class KM2; Certificate of conformity “Elakor-PTs”

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.