Izhora polyurethane sealant consists of a white paste and a transparent viscous liquid, which are mixed with a drill right before work; after mixing the compound has a pot life of at least 6 h and polymerises on average in 48 h. It fills expansion joints and butt joints of reinforced concrete, panel joints of facades and plinths, cracks, external window and door joints, and penetrations of metal, polypropylene and polyvinyl chloride pipes. The sealant is designed for 25 % joint movement, elongates by 600 % before break and serves from −65 to +90 °C. Work is carried out at air temperatures from +5 to +40 °C, with no precipitation.
| Manufacturer | Rastro (LAKHTA, SLAVYANKA, Izhora) — ZAO “Rastro”, Bolshaya Izhora |
|---|---|
| Type | joint sealants |
| Use | joints and junctions |
| Base | two-component polyurethane construction sealant: component 1 — white paste (can be tinted), component 2 — transparent viscous liquid from light yellow to brown |
| Colour | standard: white 01 (RAL 1013), grey 02 (RAL 7046), light grey 09 (RAL 7038); to order: light blue, brick red, green, pink, yellow, lilac |
| Packaging | 12.5 kg kit: component 1 — 11.25 kg plastic euro bucket, component 2 — 1.25 kg plastic container (placed inside the bucket) |
| Application method | remove loose pieces, crumbling concrete and, if necessary, old sealant; treat the joint walls with a milling cutter to a minimum filling width of 10 mm; clean with a disc brush and compressed air, dry and heat with a torch; working temperature of the sealant not lower than the air temperature; pour all of component 2 into component 1 and mix for 6…8 min with a low-speed drill of at least 1.2 kW (paddle 80 mm); place a foamed polyethylene backer rod; apply with a spatula in a layer of at least 3 mm per pass; optimum joint depth to width ratio 1 : 3; do not apply on surfaces with free moisture; dilution is not permitted; do not use on bitumen and bitumen-polymer substrates |
| Application temperature | air +5…+40 °C, no precipitation (below +5 °C — Izhora “Winter”) |
| Curing | pot life at least 6 h at (20±2) °C; full polymerisation on average 48 h |
| Key properties | pot life at (20±2) °C at least 6 h; joint movement capability 25 %; consistency 30 mm; sag resistance (20±2 °C) 2 mm; cohesive failure; nominal tensile strength at break at 20 °C 0.5 MPa; elongation at break (dumbbell specimens, 20 °C) 600 %; Fraass breaking point −65 °C; nominal stress at 100 % elongation 0.5 MPa; bond strength to concrete 0.6 MPa, to metal 0.5 MPa; water absorption over 24 h 0.5 % by weight; density 1.4±0.1 kg/l; service −65…+90 °C; UV resistance; compliance with GOST 25621-83 |
| Layer thickness | layer at least 3 mm per pass; joint width at least 10 mm |
| Consumption | 0.27 kg/linear m (joint 24 mm × layer 8 mm); R = A × B × ρ / 1,000 (ρ ≈ 1.4 kg/l) |
| Shelf life | 12 months from the date of manufacture; store at up to +30 °C in closed rooms or under a canopy, in stacks of no more than 5 tiers |
| Standards | TU 5772-026-11149403-2013; compliance with GOST 25621-83 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Two-component elastic waterproofing for structures with cracks, settlement and vibration; bridges cracks up to 1 mm without reinforcement.
Non-shrink fibre-reinforced cement mix for filling joints, butt joints and cracks in concrete; water-tightness grade W16.
Hot bitumen-polymer sealant for joints in airfield, road and bridge pavements; flexibility is retained down to −27 °C.
Cold bitumen-polymer mastic for repairing any roofs and building mastic roofs; elongation 1,500 %, service from −60 to +110 °C.
Sprayed bitumen-latex membrane for bridge decks, tunnels and flyovers; heat resistance of 260 °C allows poured asphalt to be laid on top.
Ready-to-use water-based bitumen-latex mastic for roofs, foundations and wet rooms; elongation at break 700 %.