Pakol
Pakol Remontny BK — rapid-hardening thixotropic mortar for work at −10…+7 °C
Rapid-hardening thixotropic mix for urgent repair of walls, ceilings and columns at −10…+7 °C; 12.0 MPa compressive after 2 h.
Price on request
Pakol
Pakol Litevoy BK — rapid-hardening flowable mix for the off-season, −10…+7 °C
The off-season version of the flowable mortar is designed for autumn and spring: the mix is placed at temperatures from −10 to +7 °C, and rapid strength gain gives 15.0 MPa in compression after just 2 h. The coarse-grained non-shrink material with polymer fibre is used for urgent structural repair of horizontal and slightly inclined concrete and reinforced concrete surfaces — floors, roads, airfields, bridges, equipment foundations. After 28 days: 60.0 MPa (B50), W20, F1 800, class R4.
Specifications
| Manufacturer | Pakol — OOO “NPO Pakol”, Vysokaya Gora |
|---|---|
| Type | flowable repair mortars |
| Use | floors, roads and airfields, bridges and overpasses, industrial buildings, equipment foundations |
| Base | Dry construction mix, coarse-grained, with polymer fibre, non-shrink, flowable type, on a cement binder with rapid strength gain. The mix is intended for restoration and structural repair of horizontal surfaces of concrete and reinforced concrete elements in the cold season at an ambient temperature of -10…+7 °C |
| Packaging | 25 kg bags (three-ply with a polyethylene liner) |
| Application method | For urgent structural repair of concrete and reinforced concrete structures by eliminating local damage (spalls, gouges, cavities, delaminations, etc.) from 10 to 200 mm deep on horizontal and inclined (not more than 10°) surfaces in the autumn and spring period at negative (down to -10 °C) and low positive ambient temperatures |
| Application temperature | −10…+7 °C |
| Key properties | aggregate size, mm: 3.0; mixing water, l per 1 kg: 0.12…0.15; workability: (Rk6) 26-30; bond strength to substrate, MPa: 2.5; strength after 2 h: flexural 4.0 / compressive 15.0 MPa; strength after 24 h: flexural 7.0 / compressive 30.0 MPa; strength after 28 days: flexural 9.0 (Btb5.2) / compressive 60.0 (B50) MPa; modulus of elasticity, GPa: 25.0; sulphate resistance group: III; frost resistance: F1 800, F2 300; watertightness: W20 |
| Shelf life | 12 months from the date of manufacture; storage at -40…+50 °C, humidity no more than 70 % |
| Standards | Rk6, B50, Btb5.2, W20, F1 800 to GOST 31358-2019 (taking into account the requirements of GOST R 56378-2015, class R4); TU 23.64.10-008-76310469-2021 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Other materials by Pakol
Pakol
Pakol Inektsionny V (high-strength microcement) — class B65 injection grout
High-strength microcement for injection strengthening of foundations, consolidation of structures and soil stabilisation; 85.0 MPa compressive at W/S 0.3.
Price on request
Pakol
Pakol Litevoy 400 K — coarse-grained flowable R3 mortar for deep gouges
Coarse-grained flowable class R3 mix for non-structural repair of deep gouges on floors, roads and bridges; 40.0 MPa compressive after 28 days.
Price on request
Pakol
Pakol Remontny 400 K — non-structural thixotropic R3 mortar with 3 mm aggregate
Non-structural filling of large spalls and gouges on walls, columns and beams of industrial buildings: a thixotropic R3 mix with 3 mm aggregate.
Price on request
Pakol
Pakol Remontny Zima 400 M — fine-grained antifreeze R3 mix, to −10 °C
Fine-grained R3 mix with an antifreeze admixture for filling small spalls on walls, columns and ceilings down to −10 °C without heating.
Price on request
Pakol
Pakol Remontny 800 K — high-strength thixotropic B60 mortar for strengthening
Thixotropic B60 mix with a modulus of elasticity of 27.0 GPa for strengthening reinforced concrete columns, beams and walls of buildings and bridges; flexural 12.0 MPa.
Price on request