OOO NPO Pakol (Vysokaya Gora) makes dry mixes and polymer products for repairing and strengthening concrete. Most of the range consists of the thixotropic Pakol Remontny and flowable Pakol Litevoy mortars: fine-grained M and coarse-grained K, steel-fibre KS, rapid-hardening BK and BM for the off-season and winter grades for frost down to −20 °C without heating. The Litevoy series includes mixes with strength up to 100 MPa and the fine-dispersed Mikrolitevoy.
In addition, the catalogue lists shotcrete mixes, sulphate-resistant and winter ones among them, the Pakol Finish filler, microcements for injection and soil consolidation, the Pakol Anker and Anker S grouts, and the epoxy products Epoks T for levelling, Epoks I for crack injection and Epoks P for equipment grouting.
High-strength flowable mix for grouting machine tools and equipment, installing anchors and filling joints in reinforced concrete; 80.0 MPa compressive after 28 days.
Flowable cementitious grout for high-precision grouting of equipment, anchor starter bars and joints; fibre already in the mix, 100 MPa compressive after 28 days.
Low-viscosity epoxy resin for injecting cracks 0.1–0.8 mm wide through packers in columns, beams and floors; adhesion to concrete from 3.0 MPa.
Flowable epoxy grout for high-precision installation and anchoring of industrial equipment on foundations; effective contact area at least 85 %.
Thixotropic epoxy mortar for filling spalls and gouges with a chemically resistant coating on concrete, stone and brick; 95.0 MPa compressive at 7 days.
Finely dispersed cementitious skim coat for finish repair and levelling of concrete, brick and stone walls and ceilings; bond to substrate 2.8 MPa.
Rapid-hardening microcement for injecting through and internal cracks, caverns and separations in concrete and masonry; work down to −15 °C without heating.
High-strength microcement for injection strengthening of foundations, consolidation of structures and soil stabilisation; 85.0 MPa compressive at W/S 0.3.
Coarse-grained flowable class R3 mix for non-structural repair of deep gouges on floors, roads and bridges; 40.0 MPa compressive after 28 days.
Fine-grained flowable class R3 mix for non-structural repair of shallow spalls in floors, roads and foundations; aggregate size 1.0 mm.
Coarse-grained flowable R4 mix for structural repair of floors, roads, airfields and bridges; frost resistance F1 1000, watertightness W20.
Flowable mix with steel and polypropylene fibre for repairing pavements under dynamic and vibration loads; flexural strength 11.0 MPa after 28 days.
Class R4 flowable mortar with 1.0 mm aggregate for structural repair of small spalls and cavities in industrial buildings and on airfields; W16, F1 600.
Flowable mix for fast-track structural repair of floors, roads and bridges; 20.0 MPa compressive after 2 h, workability retained for 20–30 min.
High-strength flowable mixes for structural repair of floors, roads, airfields and equipment foundations; 80.0 and 100.0 MPa compressive after 28 days.
Off-season flowable mortar for autumn and spring: placing at −10…+7 °C, 15.0 MPa after 2 h, class B50 — for floors, roads and airfields.
Steel-fibre flowable mortar for autumn and spring repair at −10…+7 °C: rapid strength gain, Btb8.0 and 60.0 MPa compressive after 28 days.
Rapid-hardening fine-grained B40 flowable mortar for autumn and spring repair of floors and equipment foundations at −10…+7 °C; 10.0 MPa after 2 h.
Coarse-grained winter B50 flowable mortar for deep gouges on bridges and equipment foundations, without heating down to −20 °C; 20.0 MPa after 2 h.
Fine grain and work without heating down to −20 °C: a mix for urgent filling of shallow spalls in road and airfield pavements; 15.0 MPa after just 2 h.
High-strength self-levelling B70 mix for winter repair of industrial floors and roads down to −20 °C; 55.0 MPa after just 24 h.
Finely dispersed flowable R4 mix for thin-layer structural repair of floors, roads and bridges; aggregate size 0.2 mm, compressive 60.0 MPa.
Basic microcement grade with particles up to 0.1 mm: it is used to prepare an injection grout for bases, soils and internal damage in masonry and concrete.
Non-structural filling of large spalls and gouges on walls, columns and beams of industrial buildings: a thixotropic R3 mix with 3 mm aggregate.
R3 mortar with grain up to 1 mm for non-structural repair of small defects in columns, beams and walls of industrial buildings at temperatures from +5 °C; B30.
Coarse-grained thixotropic R4 mortar for repair and strengthening of bridges, tunnels, dams and tanks; F1 1000, W20, compressive 65.0 MPa after 28 days.
Mix with an expansive admixture and modifiers that reduce cracking, for structural repair and strengthening of reinforced concrete; class R4, B50.
Mix with steel and polypropylene fibre for repair and strengthening of structures under dynamic and vibration loads; flexural strength 11.0 MPa (Btb8.0).
Fine-grained thixotropic R4 mortar for structural repair of shallow spalls on bridges, in tunnels and on columns; watertightness W18.
Thixotropic B60 mix with a modulus of elasticity of 27.0 GPa for strengthening reinforced concrete columns, beams and walls of buildings and bridges; flexural 12.0 MPa.
Rapid-hardening thixotropic mix for urgent repair of walls, ceilings and columns at −10…+7 °C; 12.0 MPa compressive after 2 h.
Fine-grained rapid-hardening thixotropic mix for urgent filling of shallow spalls at −10…+7 °C; 10.0 MPa compressive after 2 h.
Coarse-grained R3 mix with an antifreeze admixture for non-structural repair of walls, columns and ceilings down to −10 °C without heating.
Fine-grained R3 mix with an antifreeze admixture for filling small spalls on walls, columns and ceilings down to −10 °C without heating.
Winter B45 mix for urgent filling of spalls and cavities on walls and ceilings of dams and tanks without heating down to −20 °C; 20.0 MPa after 2 h.
Fine-grained thixotropic mortar for urgent repair of spalls and cavities on walls, columns and ceilings in frost down to −20 °C; 12.0 MPa compressive after 2 h.
High-strength winter B60 mix for repairing columns, beams and overhead areas in tunnels and on bridges down to −20 °C; 55.0 MPa after just 24 h.
Fibre-reinforced thixotropic mix for shotcreting concrete, brick and stone walls and ceilings on bridges and in tunnels; class R3, W12.
Sulphate-resistant fibre-reinforced mix for shotcreting bridges, tunnels, tanks and treatment plants; watertightness W20.
Fibre-reinforced shotcrete mix for structural repair of walls and ceilings of bridges, tunnels and tanks in frost down to −10 °C without heating.