Pakol Litevoy BKS — steel-fibre flowable mix for the off-season, −10…+7 °C
Steel-fibre flowable mortar for autumn and spring repair at −10…+7 °C: rapid strength gain, Btb8.0 and 60.0 MPa compressive after 28 days.
Price on request
Pakol
Pakol Anker S — B80 grout with steel and polymer fibre in the mix
Unlike “Pakol Anker”, this mix already contains steel and polymer fibre, and its compressive strength class is B80. The coarse-grained non-shrink flowable grout (Rk7) is used for high-precision grouting and fixing of production equipment, installation of anchor starter bars, rigid filling of joints in reinforced concrete structures and grouting under column bearing elements. After 24 h it reaches 45 MPa in compression, after 28 days 100 MPa; F1 1000, W20, class R4.
Specifications
| Manufacturer | Pakol — OOO “NPO Pakol”, Vysokaya Gora |
|---|---|
| Type | cementitious grouts |
| Use | equipment foundations, anchoring of rebar and bolts, columns and beams, industrial buildings, floors |
| Base | Dry cement mix, coarse-grained, rapid-hardening, non-shrink, flowable type |
| Packaging | 25 kg bags (three-ply valve bags with a polyethylene liner); steel and polymer fibre included in the mix |
| Application method | For high-precision grouting and fixing of production equipment, installation of anchor starter bars, rigid filling of joints in concrete and reinforced concrete structures, grouting under column bearing elements |
| Application temperature | optimum +18…+40 °C; permitted from +5 °C |
| Key properties | aggregate size: 3 mm; mixing water: 0.12–0.15 l per 1 kg; workability: Rk7 (ring spread 30–35 cm); initial setting time: ≥40 min; bond strength to substrate: 2.5 MPa; strength after 24 h: flexural 8 / compressive 45 MPa; after 28 days: flexural 14 / compressive 100 MPa; modulus of elasticity: 27 GPa; sulphate resistance group: III; frost resistance: F1 1000, F2 300; watertightness: W20; abrasion: ≤0.4 g/cm² |
| Shelf life | 12 months from the date of production; storage at −30…+50 °C, humidity no more than 70 % |
| Standards | Rk7, B80, Btb8.0, W20, F1 1000 to GOST 31358-2019 (taking into account the requirements of GOST R 56378-2015, class R4); TU 23.64.10-008-76310469-2021 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Other materials by Pakol
Pakol
Pakol Litevoy 600K FAST — flowable mix with ultra-rapid strength gain
Flowable mix for fast-track structural repair of floors, roads and bridges; 20.0 MPa compressive after 2 h, workability retained for 20–30 min.
Price on request
Pakol
Pakol Remontny Zima 800 K — high-strength winter B60 mortar for work to −20 °C
High-strength winter B60 mix for repairing columns, beams and overhead areas in tunnels and on bridges down to −20 °C; 55.0 MPa after just 24 h.
Price on request
Pakol
Pakol Litevoy 400 M — fine-grained flowable R3 mix for shallow spalls
Fine-grained flowable class R3 mix for non-structural repair of shallow spalls in floors, roads and foundations; aggregate size 1.0 mm.
Price on request
Pakol
Pakol Epoks I — epoxy injection compound for cracks and voids
Low-viscosity epoxy resin for injecting cracks 0.1–0.8 mm wide through packers in columns, beams and floors; adhesion to concrete from 3.0 MPa.
Price on request
Pakol
Pakol Torkret Zima — shotcrete mix for work in frost down to −10 °C
Fibre-reinforced shotcrete mix for structural repair of walls and ceilings of bridges, tunnels and tanks in frost down to −10 °C without heating.
Price on request