Pakol Remontny 600 M — fine-grained thixotropic R4 mix for walls and ceilings
Fine-grained thixotropic R4 mortar for structural repair of shallow spalls on bridges, in tunnels and on columns; watertightness W18.
Price on request
Pakol
Pakol Litevoy 600K FAST — flowable mix with ultra-rapid strength gain
This grouting and flowable mix with ultra-rapid strength gain is intended for fast-track structural repair: after 2 h it gives 20.0 MPa in compression, after 24 h 35.0 MPa, while remaining workable for 20–30 min. The coarse-grained non-shrink mix restores spalls, gouges, cavities and delaminations on horizontal and slightly inclined surfaces of floors, roads, airfields, bridges and equipment foundations. After 28 days: 60.0 MPa (B50), W20, F1 800, class R4.
Specifications
| Manufacturer | Pakol — OOO “NPO Pakol”, Vysokaya Gora |
|---|---|
| Type | flowable repair mortars |
| Use | floors, roads and airfields, bridges and overpasses, industrial buildings, equipment foundations |
| Base | Dry construction mix, coarse-grained, non-shrink, grouting and flowable type, on a cement binder with ultra-rapid strength gain and workability retention of 20-30 min |
| Packaging | 25 kg bags (three-ply with a polyethylene liner) |
| Application method | For fast-track structural repair of concrete and reinforced concrete structures by eliminating local damage (spalls, gouges, cavities, delaminations, etc.) from 10 to 200 mm deep on horizontal and inclined (not more than 10°) surfaces |
| Application temperature | optimum +15…+25 °C; permitted from +5 °C |
| Key properties | aggregate size, mm: 3.0; mixing water, l per 1 kg: 0.12…0.15; workability: (Rk6) 26-30; bond strength to substrate, MPa: 2.5; strength after 2 h: flexural 3.0 / compressive 20.0 MPa; strength after 24 h: flexural 6.0 / compressive 35.0 MPa; strength after 28 days: flexural 8.0 (Btb5.2) / compressive 60.0 (B50) MPa; modulus of elasticity, GPa: 25.0; sulphate resistance group: III; frost resistance: F1 800, F2 300; watertightness: W20 |
| Shelf life | 12 months from the date of manufacture; storage at -30…+50 °C, humidity no more than 70 % |
| Standards | Rk6, B50, Btb5.2, W20, F1 800 to GOST 31358-2019 (taking into account the requirements of GOST R 56378-2015, class R4); TU 23.64.10-008-76310469-2021 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Other materials by Pakol
Pakol
Pakol Torkret — fibre-reinforced R3 mix for shotcreting
Fibre-reinforced thixotropic mix for shotcreting concrete, brick and stone walls and ceilings on bridges and in tunnels; class R3, W12.
Price on request
Pakol
Pakol Remontny 600 KS — steel-fibre mortar for vibration-loaded structures
Mix with steel and polypropylene fibre for repair and strengthening of structures under dynamic and vibration loads; flexural strength 11.0 MPa (Btb8.0).
Price on request
Pakol
Pakol Anker S — B80 grout with steel and polymer fibre in the mix
Flowable cementitious grout for high-precision grouting of equipment, anchor starter bars and joints; fibre already in the mix, 100 MPa compressive after 28 days.
Price on request
Pakol
Pakol Litevoy Zima 600 M — winter flowable mix with fine aggregate, to −20 °C
Fine grain and work without heating down to −20 °C: a mix for urgent filling of shallow spalls in road and airfield pavements; 15.0 MPa after just 2 h.
Price on request
Pakol
Pakol Anker — B70 non-shrink grout for installing machine tools
High-strength flowable mix for grouting machine tools and equipment, installing anchors and filling joints in reinforced concrete; 80.0 MPa compressive after 28 days.
Price on request