Pakol Torkret S (sulphate-resistant) — R3 shotcrete mix with watertightness W20
Sulphate-resistant fibre-reinforced mix for shotcreting bridges, tunnels, tanks and treatment plants; watertightness W20.
Price on request
Pakol
Pakol Litevoy 600 KS — flowable steel-fibre mix for dynamic loads
Floors, roads, airfields, bridges and equipment foundations subject to dynamic and vibration loads are repaired with this flowable mix containing steel and polypropylene fibre. The coarse-grained non-shrink mix with rapid strength gain is intended for structural repair of spalls, gouges and delaminations on horizontal and slightly inclined surfaces. Steel fibre comes in separate 0.5 kg packs; after 28 days the mix shows 11.0 MPa in flexure (Btb8.0) and 65.0 MPa in compression (B50), class R4.
Specifications
| Manufacturer | Pakol — OOO “NPO Pakol”, Vysokaya Gora |
|---|---|
| Type | flowable repair mortars |
| Use | floors, roads and airfields, bridges and overpasses, industrial buildings, equipment foundations |
| Base | Dry construction mix, coarse-grained, with steel and polypropylene fibre, non-shrink, flowable type, on a cement binder with rapid strength gain |
| Packaging | 25 kg bags (three-ply with a polyethylene liner); steel fibre in separate 0.5 kg packs |
| Application method | For structural repair of concrete and reinforced concrete structures by eliminating local damage (spalls, gouges, cavities, delaminations, etc.) from 10 to 200 mm deep on horizontal and inclined (not more than 10°) surfaces subject to dynamic and vibration loads |
| Application temperature | optimum +18…+30 °C; permitted from +5 °C |
| Key properties | aggregate size, mm: 3.0; mixing water, l per 1 kg: 0.12…0.14; workability: (Rk6) 26-30; bond strength to substrate, MPa: 2.5; shrinkage strain: 1.0 (0.10); strength after 24 h: flexural 6.0 / compressive 30.0 MPa; strength after 28 days: flexural 11.0 (Btb8.0) / compressive 65.0 (B50) MPa; modulus of elasticity, GPa: 25.0; sulphate resistance group: III; frost resistance: F1 1000, F2 300; watertightness: W20 |
| Shelf life | 12 months from the date of manufacture; storage at -30…+40 °C, humidity no more than 70 % |
| Standards | Rk6, B50, Btb8.0, W20, F1 1000 to GOST 31358-2019 (taking into account the requirements of GOST R 56378-2015, class R4); TU 23.64.10-008-76310469-2021 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Other materials by Pakol
Pakol
Pakol Litevoy BK — rapid-hardening flowable mix for the off-season, −10…+7 °C
Off-season flowable mortar for autumn and spring: placing at −10…+7 °C, 15.0 MPa after 2 h, class B50 — for floors, roads and airfields.
Price on request
Pakol
Pakol Litevoy 400 K — coarse-grained flowable R3 mortar for deep gouges
Coarse-grained flowable class R3 mix for non-structural repair of deep gouges on floors, roads and bridges; 40.0 MPa compressive after 28 days.
Price on request
Pakol
Pakol Litevoy 800 K / 1000 K — high-strength flowable mix, classes B70 and B80
High-strength flowable mixes for structural repair of floors, roads, airfields and equipment foundations; 80.0 and 100.0 MPa compressive after 28 days.
Price on request
Pakol
Pakol Litevoy Zima 600 K — coarse-grained winter flowable mix to −20 °C, no heating
Coarse-grained winter B50 flowable mortar for deep gouges on bridges and equipment foundations, without heating down to −20 °C; 20.0 MPa after 2 h.
Price on request
Pakol
Pakol Remontny BM — fine-grained thixotropic mortar with rapid strength gain
Fine-grained rapid-hardening thixotropic mix for urgent filling of shallow spalls at −10…+7 °C; 10.0 MPa compressive after 2 h.
Price on request