Pakol Mikrolitevoy — finely dispersed flowable R4 mix for thin-layer repair
Finely dispersed flowable R4 mix for thin-layer structural repair of floors, roads and bridges; aggregate size 0.2 mm, compressive 60.0 MPa.
Price on request
Pakol
Pakol Epoks T — thixotropic epoxy compound for repair and levelling
This three-component thixotropic material based on an epoxy thermoset is used for finish levelling and filling of spalls and gouges while forming a chemically resistant coating. It is applied to concrete, stone and brick — on floors, columns and beams, in tanks and treatment plants, on bridges and in industrial buildings. In 1 day the compound reaches 75.0 MPa in compression, in 7 days 95.0 MPa; adhesion to concrete is at least 3.0 MPa, abrasion no more than 0.1 g/cm².
Specifications
| Manufacturer | Pakol — OOO “NPO Pakol”, Vysokaya Gora |
|---|---|
| Type | thixotropic repair mortars |
| Use | columns and beams, floors, tanks and treatment plants, industrial buildings, bridges and overpasses |
| Base | Three-component high-strength thixotropic levelling compound based on an epoxy thermoset |
| Colour | dark grey (after curing) |
| Packaging | kit: component A 6.6 kg (metal or polyethylene container), component B 1.3 kg, component C 25 kg (bag) |
| Application method | For finish levelling and filling of damage (spalls, gouges) up to 15 mm deep, forming a chemically resistant coating on concrete, stone and brick |
| Application temperature | +10…+30 °C (optimum +15…+25 °C) |
| Key properties | pot life at +30 / +22 / +10 °C: 50–60 / 90–120 / 120–150 min; strength after 1 day: flexural 25.0 / compressive 75.0 MPa; after 7 days: flexural 30.0 / compressive 95.0 MPa; adhesion to concrete at 7 days: ≥3.0 MPa; to metal at 7 days: ≥10.0 MPa; shrinkage at 1 day: ≤0.2 mm/m; abrasion: ≤0.1 g/cm² |
| Shelf life | 12 months from the date of manufacture |
| Standards | TU 23.99.19-007-76310469-2022 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Other materials by Pakol
Pakol
Pakol Litevoy BM — fine-grained flowable B40 mix for the cold season
Rapid-hardening fine-grained B40 flowable mortar for autumn and spring repair of floors and equipment foundations at −10…+7 °C; 10.0 MPa after 2 h.
Price on request
Pakol
Pakol Litevoy BK — rapid-hardening flowable mix for the off-season, −10…+7 °C
Off-season flowable mortar for autumn and spring: placing at −10…+7 °C, 15.0 MPa after 2 h, class B50 — for floors, roads and airfields.
Price on request
Pakol
Pakol Litevoy 600 KS — flowable steel-fibre mix for dynamic loads
Flowable mix with steel and polypropylene fibre for repairing pavements under dynamic and vibration loads; flexural strength 11.0 MPa after 28 days.
Price on request
Pakol
Pakol Remontny 600 M — fine-grained thixotropic R4 mix for walls and ceilings
Fine-grained thixotropic R4 mortar for structural repair of shallow spalls on bridges, in tunnels and on columns; watertightness W18.
Price on request
Pakol
Pakol Inektsionny V (high-strength microcement) — class B65 injection grout
High-strength microcement for injection strengthening of foundations, consolidation of structures and soil stabilisation; 85.0 MPa compressive at W/S 0.3.
Price on request