REKS® Graut GP — low-viscosity pourable grout, 75 MPa
Non-shrink low-viscosity R4 grout for machine bases and fixing beams, columns and bolts; from 35 MPa after one day and from 75 MPa at 28 days.
Price on request
REKS
REKS® AR — thixotropic R4 repair mortar for spraying and trowel application
Wet spraying and trowelling are the two application methods for REKS® AR, a non-shrink fibre-reinforced thixotropic mortar of class R4 per GOST R 56378. Unlike AR FM, it is supplied as a single 25 kg bag, without a separate pail of fibre. The mortar restores elements of bridges and overpasses, tunnels, dams, tanks and industrial buildings, prestressed beams and columns; at 28 days it reaches at least 55 MPa in compression and 7 MPa in flexure.
Specifications
| Manufacturer | REKS — OOO “SPS” |
|---|---|
| Type | thixotropic repair mortars |
| Use | bridges and overpasses, tunnels and metro, hydraulic structures and dams, industrial buildings, tanks and treatment plants, columns and beams |
| Base | non-shrink fibre-reinforced thixotropic cementitious repair mortar |
| Colour | grey |
| Packaging | bag 25 kg |
| Application method | repair of damaged elements of concrete and reinforced concrete structures by wet spraying and by trowel; repair of structures in service in a marine environment; repair of structural elements subject to repeated loading; repair of structures exposed to sulphates |
| Application temperature | +5…+30 °C |
| Key properties | modulus of elasticity: ≥25,000 MPa; density of hardened mortar: 2.3 ± 5 % t/m³; freeze-thaw resistance: F2 300; bond to substrate at 28 days: ≥2.0 MPa; water impermeability: W16; compressive strength at 28 days: ≥55 MPa; flexural strength at 1 day: ≥4 MPa; flexural strength at 28 days: ≥7 MPa; bond to substrate at 28 days after 50 freeze-thaw cycles in salts: ≥2.0 MPa; aggregate size: 1.25 mm; flowability (truncated cone spread on a flow table): 120–140 mm; flowability retention: ≥45 minutes; compressive strength at 1 day: ≥25 MPa; capillary water absorption: no more than 0.4 kg/(m²·min⁰·⁵); sulphate resistance coefficient (365 days): 0.982 % |
| Shelf life | 12 months from the date of manufacture |
| Standards | class R4 per GOST R 56378 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Other materials by REKS
REKS
REKS® Praymer Antikor — anti-corrosion rebar primer with corrosion inhibitors
One-component primer with corrosion inhibitors protecting steel rebar during repair of reinforced concrete, including where chlorides are present; 5 and 10 kg pails.
Price on request
REKS
REKS® Strukto 100 — thixotropic R4 repair mortar resistant to acidic media
Non-shrink fibre-reinforced R4 mortar for bridges, tunnels, dams and treatment plants, tested for resistance in liquid acidic aggressive media.
Price on request
REKS
REKS® Fiks Epo Tiks — epoxy-based chemical anchor for rebar and studs
Two-component epoxy chemical anchor for bonding rebar, anchors and studs of any diameter into B15–B60 concrete, stone and brick.
Price on request
REKS
REKS® Akrisil L — acrylic grout for equipment and rails, work from −10 °C
Acrylic resin grout for fixing equipment with dynamic loads and rails; applied at temperatures from −10 to +25 °C.
Price on request
REKS
REKS® R3 — class R3 repair mortar, 40 MPa, for interior and exterior work
Non-shrink thixotropic class R3 mortar for local repair and levelling of reinforced concrete in industrial buildings and tanks; compression from 40 MPa.
Price on request