SLAVYANKA coating waterproofing mastic is based on bitumen, polymers and an organic solvent and is applied cold — by roller, spatula or spraying, and on horizontal surfaces by pouring. It is used for external protection of foundations, basements, piles and tanks, on bridge elements and pipelines, and in damp non-residential rooms; it is not used inside residential premises. Work is possible at air temperatures from −10 to +50 °C if the surface is heated above zero. The coating elongates by 1,500 %, withstands bending in frost down to −42 °C and serves from −60 to +110 °C.
| Manufacturer | Rastro (LAKHTA, SLAVYANKA, Izhora) — ZAO “Rastro”, Bolshaya Izhora |
|---|---|
| Type | mastics and liquid membranes |
| Use | foundations and basements, tanks and pools, bridge structures, interiors |
| Base | one-component cold-applied solvent-based bitumen-polymer mastic (bitumen, solvent, polymers) |
| Colour | black |
| Packaging | 20 kg metal buckets |
| Application method | clean the substrate, moisture not more than 4 %, at sub-zero temperatures heat the surface above 0 °C; stir with a drill (at least 1.2 kW); if necessary, dilute with solvents (toluene, white spirit, petrol, Nefras S, Ar) up to 20 % by weight; apply by roller, spatula, airless or air spraying, on horizontal surfaces — by pouring; reinforcement with glass fabric and polyester; in hot weather in coats of no more than 0.5 mm in 4…5 passes; backfill after drying |
| Application temperature | air −10…+50 °C; surface above 0 °C; working temperature of the mastic not lower than +15 °C |
| Curing | tack-free for a 2 mm coat 24 h (+20±2 °C, relative humidity not more than 60 %); rain resistance after 1 h |
| Key properties | nominal tensile strength 1.0 MPa; elongation at break 1,500 %; bond strength to concrete 0.8 MPa, to metal 1.0 MPa, to polyurethane foam 0.8 MPa, to cement-based tile adhesive 0.7 MPa; flexibility on a R5 mm bar −42 °C; Fraass breaking point −60 °C; heat resistance 110 °C; water-tightness at 0.03 MPa — no wet spot; water absorption over 24 h 0.4 %; nominal viscosity 140…180 mm; solids content 61 %; density 1.1 kg/dm3; chemical resistance at pH 2 and pH 12 — resistant; a 1 mm film withstands 10 kV; service −60…+110 °C; do not use inside residential premises or in contact with solvents and oils |
| Layer thickness | recommended 2 mm dry film |
| Consumption | 1.39 kg/m² per 1 mm dry film |
| Shelf life | 36 months from the date of manufacture; store at no higher than +35 °C, away from direct sunlight and heating appliances |
| Standards | TU 5775-011-11149403-2003; compliance with GOST 30693-2000; G4, V3, RP4 (NPB 244-97) |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Sprayed bitumen-latex membrane for bridge decks, tunnels and flyovers; heat resistance of 260 °C allows poured asphalt to be laid on top.
Rapid-hardening cement hydraulic plug for stopping active leaks through cracks, joints and holes; sets in 1–3 min.
Mastic based on divinyl-styrene and acrylic polymers for foundations, roofs, bridges and tanks; bond to concrete and metal 2.0 MPa.
Two-component liquid rubber for mechanised spraying on foundations, tunnels, pools and roofs; elongation at break 1,500 %.
Winter polyurethane mastic for foundations, car parks and wet rooms: applied at air temperatures from −20 to +10 °C.
Elastic injection resin for sealing dry and damp cracks, joints and butt joints, including moving ones; viscosity 150 mPa·s.