WETISOL I-210 — polyacrylate compound for injection waterproofing
Wetisol (INGRI)

WETISOL I-210 — polyacrylate compound for injection waterproofing

Injection waterproofing

WETISOL I-210 is made up of three components — a methacrylic polymer, an accelerator and an initiator — and the viscosity of the main component does not exceed 4 mPa·s. The compound is used to eliminate leaks in cold and expansion joints, cracks and abutments, to create curtains behind the structure and anti-seepage curtains in soils, to cut off capillary rise of moisture and to fill cast-in injection hoses. The polymerisation time is adjusted with the accelerator within the range from 30 s to 40 min. The gel, with an elongation of at least 100%, swells in water by more than 25% and does not cause corrosion.

Specifications

ManufacturerWetisol (INGRI) — OOO “Ingri”
Typeinjection waterproofing
Useleak repair, joints and abutments, foundations and basements
Basepolyacrylate injection compound: comp. A — methacrylic polymer, comp. B — accelerator, comp. C — catalyst (initiator)
Colourcomp. A — blue liquid; comp. B — viscous liquid, colourless to brown; comp. C — white powder
Packagingcomp. A — 20 kg plastic canister; comp. B — 1 kg plastic bottle; comp. C — 0.7 kg plastic bucket
Application methodinjection waterproofing of leaks: cold and expansion joints, cracks, dewatering wells, abutments; injection behind the structure (waterproofing curtains); cut-off of capillary rise of moisture; repair of waterproofing based on polymer membranes; filling of cast-in injection hoses; soil consolidation and anti-seepage curtains in soils; two-component pump ZOGEL ZP-14P200-2K, dosing (A + B) : (C + water) = 1:1 by volume; A+B solution: add 0.1–1 kg of accelerator B to the 20 kg canister of comp. A, adjusting for temperature, shake the closed canister for 1–2 min; C+water solution: 0.7 kg of comp. C per 18 l of water, stir mechanically until dissolved; test batches under site conditions; tools — with clean water
Application temperaturestructure, water and air +5…+25 °C
Curingpolymerisation time from 30 s to 40 min (adjusted by the accelerator concentration); gel time at 22 °C: B 0.1 kg — 10 min, 0.3 kg — 3 min, 0.7 kg — 40 s, 1.0 kg — 15 s; in the cold gelation slows down
Key propertiesdensity at 23 °C: comp. A 1.1±0.05 g/cm³, comp. B 1.12±0.05 g/cm³ (GOST 31992.1); dynamic viscosity of comp. A at 23 °C max 4 mPa·s (GOST 25271); relative elongation at break at least 100% (GOST 270); on contact with water the gel increases in volume by more than 25%, without water it slowly shrinks without breaking down (reversible); does not cause corrosion; resistant to freeze/thaw cycles and water absorption/release cycles; resistant to bacterial and fungal degradation
Shelf life12 months from the date of manufacture in original packaging at +5…+35 °C indoors, protected from UV and direct sun; do not freeze
StandardsTU 2241-014-94613022-2013

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.

Other materials by Wetisol (INGRI)

Wetisol (INGRI)

Wetisol S-CP — epoxy primer for polyurea

Two-component epoxy primer for concrete and brick under Wetisol Spray sprayed polyurea; adhesion to concrete over 4.0 MPa.

Price on request
Wetisol (INGRI)

Wetisol I-212 — methacrylate injection gel

Acrylic gel for injection into joints, cracks and behind the structure; swells by more than 25% on contact with water, gel time is adjustable.

Price on request