WETISOL I-5107 FG — polyurethane injection with adjustable reaction
Wetisol (INGRI)

WETISOL I-5107 FG — polyurethane injection with adjustable reaction

Injection waterproofing

The reaction rate of WETISOL I-5107 FG is set with an accelerator: without it the resin remains workable for at least 40 min, and with 1.0% accelerator it reacts completely in 1 min 5 s. The low-viscosity two-component compound forms a watertight membrane, does not need water for polymerisation and increases in volume to a limited extent on contact with it. It is used to strengthen fractured soils, fill large voids, seal service penetrations, embedded parts, precast reinforced concrete joints and expansion joints, create horizontal cut-off barriers and strengthen brick masonry. Service — from −40 to +60 °C.

Specifications

ManufacturerWetisol (INGRI) — OOO “Ingri”
Typeinjection waterproofing
Usejoints and abutments, foundations and basements, leak repair
Basetwo-component low-viscosity polyurethane-based injection compound with adjustable reaction time (WETISOL I-5107 Accelerator); forms a watertight membrane, increases in volume to a limited extent on contact with water; no water is required for polymerisation
Colourcured — homogeneous yellowish gel or foam; comp. A — transparent or opalescent yellowish liquid; comp. B — yellowish to brownish liquid
Packaging10 kg metal buckets (A+B kit); 0.1 kg polymer bottle of WETISOL I-5107 Accelerator
Application methodincreasing the strength, stability and watertightness of soils, resin treatment of fractured soils, filling of large voids and cracks, prevention of water inflow; filling of cracks, joints and voids in above-ground and underground engineering structures; sealing of service penetrations, embedded elements, precast reinforced concrete joints, expansion joints; horizontal cut-off barrier, bonding and strengthening of brick masonry; preliminary survey of the structure; clean cracks and voids with compressed air or a high-pressure water jet; two-component pump ZOGEL ZP-14P200-2K with static mixers (30 cm spiral or a set of 20); packers Z23016, Z23005, Z23154, Z23172, Z23249; centres at a distance of ½ the element thickness, staggered at a spacing of ½ the thickness, holes at 40–50°; for cut-off barriers and membranes — holes at 90° to a depth of 1/3–2/3 of the thickness; vertical joints — from bottom to top until the pressure rises or resin comes out of the adjacent hole; A:B = 1:1 by volume; stir the accelerator and add it only to comp. A (dosage relative to the A+B mix); if viscosity increases, flush the pump with WETISOL S-Clean; tools — solvent 646
Application temperatureair and substrate +5…+30 °C; material +15…+25 °C
Curingpot life without catalyst at least 40 min; at 20 °C (accelerator, wt. %: start / working time / start of expansion / finish): 0 — 15 min / 40 min / – / over 5 h; 0.1 — 1 min 15 s / 3 min 30 s / 10 min / 25 min; 0.2 — 40 s / 2 min 15 s / 5 min / 6 min; 0.4 — 30 s / 1 min 35 s / 1 min 45 s / 2 min 20 s; 1.0 — 20 s / 50 s / 57 s / 1 min 5 s
Key propertiesdensity: comp. A 0.92±0.05 g/cm³, comp. B 1.06±0.05 g/cm³ (GOST 31992.1); ultimate tensile strength at break at least 1 MPa and relative elongation at break at least 50% (GOST 11262; for pure resin that has not been in contact with water); volume increase on contact with water up to 6 times (company method); resistance to freeze/thaw cycles, aggressive media, industrial and sea water; service temperature from −40 to +60 °C
Shelf life12 months from the date of production in unopened undamaged original containers at +5…+30 °C
StandardsTU 2257-008-94613022-13 with amendment No. 1

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.