LEVELINE FC70 S is a dry hardening mix based on Portland cement with a quartz aggregate, worked into freshly laid concrete with power trowels. It is suitable for floors in production workshops, warehouses, car parks, ramps and outdoor areas with moderate abrasion and impact loads. At 28 days its compressive strength is at least 70 MPa, abrasion is no more than 0.25 g/cm², and the service temperature range is −40 to +60 °C. The topping is not intended for acids and salts.
| Manufacturer | INDASTRO — OOO “Sedrus” |
|---|---|
| Type | toppings |
| Use | production workshops, warehouses and logistics, car parks and ramps, outdoor areas |
| Base | Portland cement, quartz aggregate |
| Packaging | 25 kg bag |
| Application method | dry application onto freshly laid concrete (~2/3, then ~1/3 of the consumption) with floating by power trowels with a disc, then finishing with blades; curing — LEVELINE SP2 compound |
| Application temperature | substrate and air above +10 °C; not recommended above +30 °C and/or at humidity below 60% |
| Key properties | Compressive strength at 28 days at least 70 MPa; abrasion no more than 0.25 g/cm2; max. aggregate size 2.5 mm; service temperature -40…+60 °C; intensity of mechanical impact (SNiP 2.03.13) — significant; exposure to liquids — high |
| Consumption | 4 - 6 kg/m2 |
| Shelf life | 12 months from the date of manufacture (dry room, original factory packaging) |
| Standards | manufacturer's TU; impact intensity per SNiP 2.03.13 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Fibre-reinforced mortar with sand up to 0.63 mm for repair and finishing of concrete structures of bridges, treatment plants and underground facilities; W12.
Thixotropic R4 mortar for repairing high-strength concrete and reinforced concrete of B50 and above; 70 MPa at 28 days, water impermeability W20.
Flowable R4 mortar for structural repair of B60 concrete and above; at least 35 MPa after 24 hours and 80 MPa after 28 days.
Cementitious grout for installing equipment, columns, joints and anchors at low temperatures; 10 MPa after 6 hours at −10 °C, 50 MPa at 28 days.
Fibre-reinforced finishing mortar for fine finishing of concrete structures in winter at temperatures from −10 to +10 °C; compressive strength 40 MPa at 28 days.
Thixotropic R4 repair mortar for high-strength concrete structures; at least 30 MPa after 24 hours and from 60 MPa after 28 days.