The corundum aggregate makes FC80 Cr a more wear-resistant dry-shake topping option: abrasion no more than 0.15 g/cm², compressive strength at 28 days at least 80 MPa. The mix is applied by the dry method onto fresh concrete of class no lower than B22.5 and floated with power trowels. It is designed for high abrasion and moderate impact loads indoors and outdoors and withstands service from −50 to +200 °C. Acids and salts are contraindicated for it.
| Manufacturer | INDASTRO — OOO “Sedrus” |
|---|---|
| Type | toppings |
| Use | production workshops, warehouses and logistics, car parks and ramps, outdoor areas |
| Base | Portland cement, corundum aggregate |
| Packaging | 25 kg bag |
| Application method | dry application onto freshly laid concrete (~2/3, then ~1/3 of the consumption) with floating by power trowels, finishing; curing — LEVELINE SP2 compound; joint cutting no later than one day after |
| Application temperature | substrate and air above +10 °C; not recommended above +30 °C and/or at humidity below 60%; concrete of class no lower than B22.5 |
| Key properties | Compressive strength at 28 days at least 80 MPa; abrasion no more than 0.15 g/cm2; max. aggregate size 3 mm; service temperature -50…+200 °C; intensity of mechanical impact (SNiP 2.03.13) — very significant; exposure to liquids — high |
| Consumption | 4 - 6 kg/m2 |
| Shelf life | 12 months from the date of manufacture |
| Standards | manufacturer's TU; impact intensity per SNiP 2.03.13 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Fibre-reinforced mortar with sand up to 0.63 mm for repair and finishing of concrete structures of bridges, treatment plants and underground facilities; W12.
Black conductive epoxy primer for antistatic floors in electronics, laboratories, cleanrooms and data centres; class KM2.
Two-component epoxy coating protecting concrete of treatment plants and sewers against sulphuric acid and hydrogen sulphide; contact with drinking water is permitted.
Thixotropic R4 repair mortar for structures made of B60 concrete and above; compressive strength at 28 days at least 80 MPa, flexural strength 10 MPa.
Ultra-rapid-hardening R4 grout for equipment, anchors and sleepers in track concrete; 10 MPa in compression after just 2 hours.
Pourable hardening mortar for fresh concrete and for repairing worn floors in workshops and warehouses; abrasion class AR1 to EN 13892-4.