LEVL Coat 304 RAPID — fast-curing epoxy self-levelling floor
LEVL (INGRI)

LEVL Coat 304 RAPID — fast-curing epoxy self-levelling floor

Epoxy floors

If a floor must be put into service within a day, LEVL Coat 304 RAPID is chosen: at +20 °C it withstands light loads after about 6 hours and full loads after 12 hours. The coloured gloss epoxy compound is laid as a self-levelling or highly filled coating over LEVL Coat 101, 103 or 104 RAPID primers. After one day Shore D hardness is at least 70, Taber abrasion up to 60 mg, adhesion from 2.5 MPa. It suits warehouses, assembly shops, workshops, loading areas, covered car parks, schools and healthcare facilities.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Usewarehouses and logistics, production workshops, car parks and ramps, retail and public buildings, food and pharmaceutical, chemically resistant
Baseepoxy resin (two-component coloured material, fast-curing)
Colourcoloured (wide range of colour options); gloss finish
Packagingkits (A+B) of 25 kg; 2.4 kg; A : B = 2.82 : 1; polymer : filler = 1 : 0.7
Application methodself-levelling and highly filled coatings on cementitious substrates with high wear loads; over LEVL Coat 101/103/104 RAPID primer (moisture up to 5 %) or 106M (up to 10 %); pouring, squeegee or notched trowel, rolling with a spiked roller after 5 min; can be overcoated with a UV-resistant finish
Application temperatureair and substrate +10…+30 °C; optimally, components and substrate +15…+25 °C; air humidity no more than 80 %; substrate moisture no more than 5.0 % by weight (primers 101/103/104 RAPID) or 10.0 % by weight (106M); 3 °C above the dew point
Curinglight loads: +10 °C ~12 h, +20 °C ~6 h, +30 °C ~4 h; foot traffic: ~16 / ~8 / ~6 h; full loads: ~24 / ~12 / ~8 h; next coat after 8–48 h at +20 °C
Key propertiesShore D hardness at least 50 (after 6 h), at least 70 (after 1 day); Taber abrasion resistance (CS10/1000 g/1000 rev.) no more than 60 mg (after 1 day); adhesion (over LC 101 primer) at least 2.5 MPa (after 1 day); mix density 1.36 ± 0.05 g/cm³; non-volatile content at least 95 %; pot life +10 °C 60 min, +20 °C 30 min, +30 °C 15 min; service temperature from −10 to +60 °C (highly filled: short-term up to +90 °C, hot-water washing); chemical resistance: on request
Layer thicknessadmissible 1.5–5.0 mm; recommended 2.0 mm
Consumptionmain layer 1.5 mm: LEVL Coat 304 RAPID 1.5 kg/m² + quartz sand 0.1–0.3 mm 1.0 kg/m²; theoretical consumption (polymer + filler) 1.67 kg/m² per 1 mm
Shelf life12 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-006-94613022-06 with Amendment No. 1; substrate per SP 71.13330.2017 cl. 8.12.2; test methods GOST 31992.1, GOST 31939, GOST 28574, GOST 24621

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.