LEVL Coat 573 — main layer of a methyl methacrylate floor with coloured sand
LEVL (INGRI)

LEVL Coat 573 — main layer of a methyl methacrylate floor with coloured sand

Methyl methacrylate floors

The main layer of the MMA system, LEVL Coat 573, makes the floor ready for full load in about one day at +20 °C, and installation is possible at temperatures down to −10 °C. The colourless carboacrylate resin is spread with a squeegee over LEVL Coat 171 primer and broadcast to excess with coloured quartz sand or smoothed with a trowel; the finish is LEVL Coat 271. The coating resists chemicals, water, UV and bacteriological attack and operates from −30 to +60 °C. It is used in warehouses, workshops, car parks and helipads, food and wet rooms, and sales floors.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typemethyl methacrylate (MMA) floors
Usewarehouses and logistics, production workshops, car parks and ramps, retail and public buildings, wet rooms, food and pharmaceutical, chemically resistant, decorative, outdoor areas
Basecolourless carboacrylate (MMA) resin; LEVL Coat 070 catalyst, at sub-zero temperatures LEVL Coat 075 accelerator
Colourmatches the colour of the filler (coloured quartz sand); tinting with dry mineral pigment
Packaging1 kg metal can; 10 and 20 kg metal pails; 200 kg steel drum; LEVL Coat 070 catalyst depending on temperature: −10 °C 4.5 % (+ accelerator 2 %), 0 °C 3.5 % (+2 %), +10 °C 3 % (+1 %), +20 °C 3 %, +30 °C 1 % (by weight)
Application methodrigid-elastic highly filled coatings with coloured wear-resistant filler on concrete and screeds, indoor and outdoor work: over LEVL Coat 171 primer, main layer by squeegee + broadcast to excess with coloured sand (textured) or smoothing with a trowel (smooth-textured), finish LEVL Coat 271; next coat after ~1 h
Application temperatureair and substrate from −10 °C to +30 °C; material +5…+30 °C (optimum +17…+23 °C); air humidity no more than 80 %; substrate moisture no more than 5.0 % by weight; 3 °C above the dew point; below 0 °C, with LEVL Coat 075 accelerator; supply and exhaust ventilation required
Curingfoot traffic: −10 °C ~24 h, 0 °C ~12 h, +10 °C ~6 h, +20 °C ~4 h, +30 °C ~2 h; light loads: ~48 / ~48 / ~12 / ~12 / ~6 h; full strength gain: ~4 / ~3 / ~2 / ~1 days / ~12 h; pot life ~13–25 min, curing ~30–60 min
Key propertiesStrength when mixed with quartz sand 1:4 (for reference): compressive 26 MPa, flexural 14 MPa; ultimate tensile strength at least 11 MPa; relative elongation at least 4 %; Shore D hardness (7 days) at least 39; adhesion (over LEVL Coat 171 primer) at least 2.5 MPa; density 0.95 ± 0.05 g/cm³; non-volatile content at least 97 %; high resistance to aggressive chemicals, water, UV and bacteriological attack; service temperature from −30 °C to +60 °C, short-term up to +90 °C
Layer thickness1.4–12.0 mm (mixed with quartz sand); in systems, the design wearing layer is 4.0 mm
Consumptionoption A (textured, 4.0 mm): LEVL Coat 573 1.6 kg/m² + LEVL Coat 070 0.048 kg/m² + coloured quartz sand 0.1–0.4 mm 1.39 kg/m² + 0.8–1.2 mm 4.37 kg/m², finish LEVL Coat 271 0.7 kg/m² + 070 0.014 kg/m²; option B (smooth-textured, 4.0 mm): 573 1.36 kg/m² + 070 0.041 kg/m² + sand 0.8–1.2 mm 5.44 kg/m², finish 271 1.00 kg/m² + 070 0.020 kg/m²; primer 171 0.4 kg/m² + 070 0.008 kg/m² + sand 1.0 kg/m²
Shelf life6 months from the date of manufacture (in unopened packaging); recommended storage temperature +15…+25 °C
StandardsTU 2257-039-94613022-15; test methods GOST 31992.1, GOST 11262, GOST 24621, GOST 31939, GOST 28574, GOST 310.4

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.