This quartz-filled two-component compound flows into a glossy coating for workshops, warehouses, car parks and sales floors with impact and vibration loads. It is spread with notched squeegee rakes or trowels over a substrate primed and levelled with “Elakor-PU” materials. Compressive strength is 42 MPa, Shore D hardness 53–58, service temperature from −60 to +80 °C; pouring is carried out at air and substrate temperatures from +5 to +22 °C.
| Manufacturer | Elakor — OOO “TEOKHIM-PROM”, Moscow Region |
|---|---|
| Type | polyurethane floors |
| Use | production workshops, warehouses and logistics, car parks and ramps, retail and public premises, chemically resistant, wet rooms |
| Base | self-levelling two-component polyurethane compound; composition: urethane prepolymers, polyols, pigments and fillers, functional additives |
| Colour | coloured; gloss |
| Packaging | Component “A” 26.5 kg + Component “B” 3.5 kg = Kit 30 kg |
| Application method | Self-levelling coatings on concrete and other mineral surfaces in premises with increased mechanical, impact and vibration loads. On surfaces primed and levelled with “Elakor-PU” materials. Squeegee rakes with notched blades, notched trowels (gauge rakes with adjustable gap are not permitted). Surface moisture not more than 4 wt%, relative air humidity not more than 80%, dew point +3°C, waterproofing on the lowest floors. |
| Application temperature | material from +15°C to +20°C |
| Curing | pot life of the mix on the surface at (20±2)°C at least 30 min; drying to degree 3 at (20±2)°C – not more than 10 h |
| Key properties | A:B ratio by weight 7.5:1; solids content at least 100%; mix density 1.7±0.02 kg/l; service temperature -60°C ... +80°C, short-term (up to 30 min) up to +140°C; compressive strength 42 MPa (GOST 4651-2014, ISO 604:2002); film tensile strength at least 12 MPa; elongation at least 10%; impact strength (U-2M) 100 cm; flexibility (bend test) not more than 4 mm; Shore D at 28 days 53-58; Taber abrasion SC-10, 1000 g, 28 days – 19 mg; gloss at 60° 85-90 (gloss); conventional lightfastness (onset of chalking) at least 100 h; fire hazard class KM2; chemical resistance: water, salt and alkali solutions of any concentration, acid solutions up to 10-20%, oils and fats of all kinds, organic solvents, petrol, diesel fuel |
| Consumption | 1.7 kg/m² per 1 mm of coating thickness |
| Shelf life | 8 months in the manufacturer's original packaging; store and transport at temperatures from 0°C to +25°C |
| Standards | Certificate of conformity (fire safety) “Elakor-PU 2K”; ROSTEST letter “Elakor-PU 2K”; MOSGOSEKSPERTIZA letter on the use of “Elakor-PU 2K” at garage facilities |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Professional version of the one-component polyurethane primer: impregnation and priming of concrete under polyurethane coatings at temperatures down to −30 °C.
Self-levelling polyurethane-cement coating for floors with moderate and significant abrasive, impact and vibration loads.
Highly elastic polyurethane self-levelling floor with 120 % elongation for sports halls, stadiums, shooting ranges and van floors.
Elastic gloss polyurethane varnish for the finishing coat of elastic and sports floors and floors with vibration loads.
Matt polyurethane varnish with a UV filter for the finishing protection of epoxy and polyurethane floors, parquet and plastic.
Semi-matt transparent polyurethane varnish with a UV filter for protecting polymer floors from ultraviolet and wear.