Elakor-PU Self-levelling Floor Rubber — highly elastic sports self-levelling floor
ELAKOR

Elakor-PU Self-levelling Floor Rubber — highly elastic sports self-levelling floor

Polyurethane floors

The softest self-levelling floor of the range: Shore D hardness 25–35, elongation at break 120 %. It is poured over rubber mats and crumb, concrete, sand concrete, wood or metal, spread with a notched squeegee rake and rolled with a spiked roller. According to the technical data sheet, the coating is intended for sports halls, stadiums, outdoor sports grounds, shooting ranges, industrial premises with impact loads, and floors of vans and mobile units; the colour is selected from the RAL chart.

Specifications

ManufacturerElakor — OOO “TEOKHIM-PROM”, Moscow Region
Typepolyurethane floors
Useproduction workshops, retail and public premises, chemically resistant
Basetwo-component polyurethane compound for highly elastic coatings (solids content ~ 100%); composition: urethane prepolymers, hardener, functional additives
Colourcoloured; colour selection – from the RAL chart
PackagingComponent “A” 16 kg + Component “B” 5 kg = Kit 21 kg
Application methodSelf-levelling sports and highly elastic floors of specified hardness (Shore D 25-35) on rubber mats and crumb, concrete, sand concrete, wood, metal. Concrete at least M200, cured for at least 28 days, moisture not more than 4 wt%, evenness – not more than 4 mm under a 2 m straightedge, slope not more than 0.5%, damping strip at the walls, movement joints to be repeated; relative air humidity not more than 80%, dew point +3°C. Squeegee rake with a notched blade or notched trowel, rolling with a spiked roller.
Application temperatureair and surface: from +5°C to +22°C; materials from +15°C to +20°C
Curingpot life of the mix on the surface at (20±2)°C at least 30 min; drying to degree 3 at (20±2)°C – not more than 10 h
Key propertiesA:B ratio by weight 3.2:1; solids content ~100%; mix density 1.2 kg/l; mix viscosity (VZ-6 cup) at +20°C 37 s; service temperature -60°C ... +80°C, short-term (up to 30 min) up to +140°C; compressive strength 42 MPa (GOST 4651-2014, ISO 604:2002); film tensile strength at least 12 MPa; elongation 120%; impact strength (U-2M) 100 cm; flexibility (bend test) not more than 1 mm; Shore D at 28 days 25-35; Taber abrasion SC-10, 1 kg, 28 days – 17 mg; gloss at 60° 80-90; fire hazard class KM2; chemical resistance: water, salt and alkali solutions of any concentration, acid solutions up to 10-20%, oils and fats of all kinds, organic solvents, petrol, diesel fuel
Layer thicknessmaximum application thickness per coat – not more than 3 mm
Consumption1.2 kg per 1 mm of layer thickness (A+B mix)
Shelf life8 months in the manufacturer's original packaging; store and transport at temperatures from 0°C to +25°C
StandardsCertificate of conformity (fire safety) “Elakor-PU 2K”; ROSTEST letter “Elakor-PU 2K”

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.