Wetisol S-MP2 — zinc-rich primer for metal
Wetisol (INGRI)

Wetisol S-MP2 — zinc-rich primer for metal

Other waterproofing materials

Wetisol S-MP2 is a one-component zinc-filled polyurethane compound: it primes steel before Wetisol polycarbamide coatings and at the same time protects it from corrosion through a galvanising effect. The primer is used on tanks, metal fencing of water bodies, bridge supports, ship decks and hulls, drilling platforms and metal roofs. Work is possible at temperatures from −15 to +40 °C and air humidity of 30–98%, and the coat dries to degree 3 in no more than 2 h. Packaging — metal buckets of 1, 10 and 25 kg.

Specifications

ManufacturerWetisol (INGRI) — OOO “Ingri”
Typewaterproofing material
Baseone-component zinc-filled polyurethane-based material for priming and anti-corrosion protection of metal; cures with air moisture
Colourhomogeneous grey suspension
Packagingmetal bucket 1 kg, 10 kg, 25 kg
Application methodpriming and anti-corrosion treatment of steel surfaces before Wetisol polycarbamide coatings: tanks, metal fencing of water bodies, bridge supports, ship decks and hulls, drilling platforms, metal roofs, rolling stock and equipment; abrasive blast cleaning to degree 2 per GOST 9.402 / Sa 2½ per ISO 8501-1, Rz > 60 µm, dust level per EN ISO 8502-3 class 2–3, salts less than 10 mg/cm², no acid reaction (pH<5); mix thoroughly before use, if necessary dilute with solvent 647 (GOST 18188-72) by no more than 5%; 1–2 coats by brush, velour roller (ZOGEL Z360-2241) or airless sprayer (ZOGEL ZP-1E300, ZP-4E240); flush the pump with WETISOL S-Clean, tools with solvent 646
Application temperatureambient air and substrate from −15 to +40 °C (+10…+30 °C recommended); material temperature +10…+30 °C (+15…+30 °C recommended); relative air humidity 30–98%; 3 °C above the dew point
Curingdrying time to degree 3 max 2 h (GOST 19007); next coat — after full cure, no later than 24 h (at +20±2 °C, 65±5%); at sub-zero temperatures — double the drying time until tack-free
Key propertiesdensity at 23 °C 2.75–2.90 g/cm³ (GOST 31992.1); dry residue 86–89 wt. % (GOST 31939); drying time to degree 3 max 2 h (GOST 19007); cross-cut adhesion max 1 point (GOST 15140, method 2); zinc particles provide a galvanising effect; resistance to chemical attack and abrasion; service temperature from −60 to +60 °C (short-term up to +90 °C)
Layer thicknessdry film thickness per coat 60–100 µm (80 µm recommended)
Consumptiontheoretically 370 g/m² per 80 µm; 0.4 kg/m² by roller in 1 pass
Shelf life12 months from the date of manufacture in unopened containers at −40…+40 °C, protected from precipitation and direct sun
StandardsTU 2312-035-94613022-14 with amendment No. 1; fire safety — not subject to mandatory certification (decision No. 364-R3/15 dated 12.08.15)

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.

Other materials by Wetisol (INGRI)

Wetisol (INGRI)

Wetisol Spray 400 — hot-spray polyurea

Sprayed polyurea for foundations, tanks, roofs and bridges: a seamless membrane with 350–450% elongation, working from −60 to +90 °C.

Price on request
Wetisol (INGRI)

Wetisol I-212 — methacrylate injection gel

Acrylic gel for injection into joints, cracks and behind the structure; swells by more than 25% on contact with water, gel time is adjustable.

Price on request
Wetisol (INGRI)

Wetisol S-CP — epoxy primer for polyurea

Two-component epoxy primer for concrete and brick under Wetisol Spray sprayed polyurea; adhesion to concrete over 4.0 MPa.

Price on request