Izhora DM-65 emulsion is sprayed with a two-channel unit together with a calcium chloride-based hardener solution, and after 5 s the membrane gains 75 % of its strength. It is used to waterproof reinforced concrete bridge slabs, steel orthotropic deck plates of spans, tunnels, flyovers, overpasses and pedestrian underpasses, and as a crack-arresting interlayer on concrete and asphalt concrete. Heat resistance of 260 °C allows hot asphalt mixes, including poured asphalt, to be laid over the membrane. The coating elongates by 1,500 % before break and works from −65 to +260 °C.
| Manufacturer | Rastro (LAKHTA, SLAVYANKA, Izhora) — ZAO “Rastro”, Bolshaya Izhora |
|---|---|
| Type | mastics and liquid membranes |
| Use | bridge structures, tunnels and metro |
| Base | two-component cold-applied bitumen-polymer compound: component A — bitumen-latex emulsion, component B — hardener (calcium chloride 90–99 %) |
| Colour | component A dark brown; membrane black |
| Packaging | component A — plastic drums of 60 and 220 kg or 1,000 kg plastic IBCs; component B — 2.5 kg polyethylene bags |
| Application method | mechanised spraying only, with two-channel equipment (SLAVIANKA Rubber Spray or equivalent, preferably with diaphragm pumps); solution of component B 5 % (up to 10 %); ratio A / solution B 8/1; substrate sound, even, dry (recommended moisture not more than 8 %), fillets of LAKHTA basic repair compound or RS; concrete with hardening accelerators — prime with component A; clean metal of rust by sandblasting or with an angle grinder and degrease; second coat — after the first has dried; reinforcement with glass fabric if necessary; if the asphalt cannot be laid with a pneumatic-tyred paver — a reinforced screed over the membrane; vehicle traffic on the coating — on pneumatic tyres only; do not apply in rain |
| Application temperature | surface and air not lower than +5 °C; component A not lower than +5 °C |
| Curing | 75 % strength gain 5 s after application; rain resistance after 10 min |
| Key properties | nominal viscosity 12 s; weight fraction of residue on sieve No. 014 — 0.14 %; needle penetration 22 (0.1 mm); elasticity at 800 % elongation — 90 %; nominal tensile strength 0.5 MPa; elongation at break 1,500 %; bond strength to concrete 1 MPa; water absorption over 24 h not more than 0.4 %; flexibility on a R 5±0.2 mm bar −25 °C; softening point (heat resistance) 260 °C — allows hot asphalt mixes, incl. poured asphalt, to be laid on top; water-tightness at 0.01 MPa for 24 h — no wet spot; increase in water-tightness of the concrete substrate under positive pressure up to 20 atm; solids content 62 %; Fraass breaking point −65 °C; service −65…+260 °C; hazard class 4, non-combustible; application rate up to 1,000 m² per shift |
| Consumption | 5.1 kg/m² for a 3 mm dry film coat (as component A) |
| Shelf life | 12 months from the date of manufacture; store at +5…+35 °C; do not freeze component A |
| Standards | TU 5775-040-11149403-2016; compliance with GOST 30693-2000; works according to SP 46.13330.2012 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Two-component elastic waterproofing for structures with cracks, settlement and vibration; bridges cracks up to 1 mm without reinforcement.
Hydro-active polyurethane resin for stopping active leaks in cracks and joints by injection; foams up to 30 times its volume on contact with water.
Elastic injection resin for sealing dry and damp cracks, joints and butt joints, including moving ones; viscosity 150 mPa·s.
Hot-applied bitumen-rubber mastic for insulating pipelines, tanks and building structures against moisture and corrosion.
Two-component polyurethane sealant for expansion joints in reinforced concrete, facade panel joints and pipe penetrations; elongation 600 %.
Polyurethane resin-foam that stops a leak and elastically seals cracks and joints with one compound, including under vibration.