The one-component solvent-borne primer-enamel based on a modified acrylic resin dries quickly: dust-free in max. 0.5 h, tack-free in max. 1 h at 20 °C. It is used as a stand-alone matt coating for steel structures and bridges in UKhL1 and KhL1 climates, and also as a finish over the ANTIPLAM-1 fire protection compound. Manual cleaning to St 2 and application over a firmly adhering old coating are permitted, for local repairs from −25 °C; the coating service life according to the VNIIZhT conclusion is 10 years.
| Manufacturer | Snezhinskie Kraski — OOO “ZLKS”, Yekaterinburg |
|---|---|
| Type | primer-enamels |
| Use | steel structures, bridges |
| Base | one-component, modified acrylic resin; solvent-borne, fast-drying |
| Colour | to the RAL catalogue; matt coating |
| Application method | airless spray (nozzle 0.28–0.43 mm, 15–25 MPa); air spray (nozzle 1.7–3.0 mm, 0.25–0.3 MPa); roller; brush; solvent “SK-PUR” up to 10 % / 20 % |
| Application temperature | from −10 to +40 °C (from −25 °C for local repairs); relative humidity max. 80 %; surface 3 °C above the dew point |
| Drying | dust-free max. 0.5 h, tack-free max. 1 h at 20 °C; next coat after drying to degree 3; maximum interval up to 3 months; full cure 7 days (3 days with hot drying) |
| Compatible materials | stand-alone coating (UKhL1, KhL1); finish over the ANTIPLAM-1 fire protection composition (GF-021 + ANTIPLAM-1 + SK-AKRIL system) |
| Shelf life | 24 months from the date of manufacture; storage from −40 to +40 °C in the manufacturer’s sealed containers |
| Standards | TU 2312-046-51472338-2016; STO-01393674-007-2022 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Paste-like polyurethane for manual repair of local defects in the MASTIKOR coating in the factory and in the field, adhesion to steel at least 7.0 MPa.
Polyurethane RAL enamel for steel structures and bridges, withstands +150 °C in a dry environment, finish of C5-I and C5-M systems per ISO 12944.
Epoxy primer-enamel with micaceous iron oxide for tanks, bridges and equipment, works as a stand-alone, intermediate or primer coat.
Epoxy compound for internal protection of tanks with crude oil, fuel oil, oils and water, resistant to the stored product up to +90 °C.
Semi-gloss RAL enamel for bridges and chemical plants; in a system with SK-EPOKSID-MIO it lasts 10 years in a urea environment.
Polyurethane topcoat to the RAL catalogue for tanks, pipelines and bridges, included in the OVP register of PJSC Transneft.