The SK-PROTEKT enamel based on a lightfast aliphatic polyisocyanate forms a semi-gloss coating of at least class IV per GOST 9.032 that is resistant to UV radiation. It is applied over the SK-PROTEKT primer, the zinc-rich SK-TSINK and SK-EPOKSID-TS, over SK-EPOKSID-MIO, and on concrete over the penetrating SK-BETON. The enamel is included in the “Technological guidelines for painting steel structures of railway bridges” of JSC RZD; the SK-EPOKSID-MIO + SK-PROTEKT system is designed for OM-1 and OM-3 conditions, including a urea environment, for 10 years.
| Manufacturer | Snezhinskie Kraski — OOO “ZLKS”, Yekaterinburg |
|---|---|
| Type | polyurethane enamels |
| Use | steel structures, bridges, concrete, oil and gas, equipment, chemical plants |
| Base | two-component polyurethane; hardener — lightfast aliphatic polyisocyanate |
| Colour | to the RAL catalogue; semi-gloss coating |
| Application method | airless spray (nozzle 0.28–0.43 mm, 16–45 MPa); air spray (nozzle 1.7–3.0 mm, 0.25–0.4 MPa); roller; brush; solvent “SK-PUR” up to 5 % / 15 % / 10 % |
| Application temperature | from −10 to +40 °C (from +5 to +40 °C recommended); relative humidity max. 80 %; surface 3 °C above the dew point |
| Drying | pot life at least 2 h; dust-free max. 1.5 h, tack-free max. 4 h at 20 °C; next coat after drying to degree 3; maximum interval up to 6 months; full cure 7 days (3 days with hot drying) |
| Compatible materials | topcoat over polyurethane or epoxy primers: SK-PROTEKT primer; SK-TSINK; SK-EPOKSID-TS; SK-EPOKSID-MIO; on concrete — SK-BETON |
| Shelf life | 24 months from the date of manufacture; storage from −40 to +40 °C in the manufacturer’s sealed containers |
| Standards | TU 2312-024-51472338-2015; GOST 7409-2018; STO-01393674-007-2022; STO-01393674-008-2021 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Clear polyurethane impregnation for the concrete of bridges, tunnels and floors, applied from −20 to +50 °C at concrete moisture up to 12 %.
Epoxy primer-enamel with micaceous iron oxide for tanks, bridges and equipment, works as a stand-alone, intermediate or primer coat.
Polyurethane zinc-rich primer for bridges, tanks and marine structures, at least 80 % zinc in the coating, applied from −15 °C.
Polyurethane topcoat to the RAL catalogue for tanks, pipelines and bridges, included in the OVP register of PJSC Transneft.
Epoxy compound for internal protection of tanks with crude oil, fuel oil, oils and water, resistant to the stored product up to +90 °C.
Two-component polyurethane primer for metal, concrete and reinforced concrete, permitted for containers with bulk food products.