Where reinforcement is too congested for hand application, the flowable Profskrin RC60 RLq is used. This high-strength non-shrink mix with polymer fibre, class R4 to EN 1504, is also suitable for bridges, road pavements, airfields and car parks, and for monolithic joining of joints in concrete and reinforced concrete structures. After 2 hours it reaches 20 MPa in compression, after 28 days at least 60 MPa, in flexure 9 MPa; it can be placed at temperatures from −10 to +35 °C.
| Manufacturer | INDASTRO — OOO Sedrus |
|---|---|
| Type | flowable repair mortars |
| Use | bridges and overpasses, roads and airfields |
| Base | High-strength non-shrink flowable-type dry mix with polymer fibre |
| Packaging | bags 25 kg |
| Application method | Profskrin RC60 RLq repair mortar is used for structural repair of concrete structures: Heavily reinforced surfaces where hand application is impossible; Bridge structures; Road pavements, airfields, car parks; For monolithic joining of joints in concrete and reinforced concrete structures |
| Application temperature | −10…+35 °C |
| Key properties | mixing water: 0.15-0.16; compressive strength at 2 h: ≥20 MPa; compressive strength at 24 h: ≥25 MPa; compressive strength at 28 days: ≥60 MPa; flexural strength at 2 h: ≥4 MPa; flexural strength at 24 h: ≥5 MPa; flexural strength at 28 days: ≥9 MPa; bond strength to substrate: ≥2 MPa; workability retention: 10-15 min; frost resistance: ≥300 cycles; Mortar density, kg/m³: 2,100; maximum aggregate size, mm: 2.5 |
| Shelf life | 12 months in the original factory packaging from the date of manufacture, in a dry room |
| Standards | class R4 to EN 1504 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Elastic polyurethane self-levelling floor for workshops, warehouses, offices and schools; elongation at break from 40%, service from −60 to +80 °C.
Ultra-rapid-hardening R4 grout for equipment, anchors and sleepers in track concrete; 10 MPa in compression after just 2 hours.
Thixotropic R4 mortar for repairing high-strength concrete structures in winter, at temperatures from −10 to +10 °C; 60 MPa in compression at 28 days.
Thixotropic R4 repair mortar for high-strength concrete structures; at least 30 MPa after 24 hours and from 60 MPa after 28 days.
Moisture-curing polyurethane primer for polymer floors and stand-alone impregnation of concrete in workshops and warehouses; fire hazard class KM1.
Flowable R4 repair mortar with polymer fibre for work at −10…+10 °C on bridges, treatment plants and underground structures; 45 MPa at 28 days.