LEVL Coat 211 AS — antistatic epoxy floor paint

Epoxy floors

LEVL Coat 211 AS epoxy paint gives a thin antistatic layer without a special conductive primer: it is applied over LEVL Coat 101 primer and a copper circuit. Its second purpose is repairing LEVL Coat 309 AS and 311 AS antistatic floors without reinstalling the earthing circuit. Electrical resistance is 10⁶–10⁹ ohm, Taber abrasion up to 70 mg, fire hazard class KM2. It is produced in grey only (about RAL 7040) and suits oil refining, chemicals, electronics, aircraft hangars, laboratories and healthcare facilities.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Useantistatic/conductive, warehouses and logistics, production workshops
Basebisphenol A epoxy resin with conductive additives + amine hardener
Colourgrey (~ RAL 7040), produced in grey only; textured surface
Packagingkit A+B = 5 kg (A: 3 l metal pail, B: 3 l metal can); A : B = 2.24 : 1 (by weight)
Application methodantistatic paint coating for concrete substrates, either on its own (over LEVL Coat 101 primer and a copper circuit, without a special conductive primer) or for repairing LEVL Coat 309AS / 311AS antistatic floors without reinstalling the circuit; velour roller, no more than three coats
Application temperatureair and substrate +10…+30 °C (recommended +15…+25 °C); material +15…+30 °C (recommended +18…+25 °C); air humidity 40–80 %; substrate moisture no more than 5.0 % by weight (primer 101) or 10.0 % by weight (106M, 102W); 3 °C above the dew point
Curinglight foot traffic: +10 °C ~1 day, +20 °C ~12 h, +30 °C ~8 h; light loads ~4 / ~2 / ~1 day; full strength gain ~8 / ~6 / ~4 days; next coat after 12–48 h at +20 °C
Key propertiesElectrical resistance 10^6–10^9 ohm (GOST R 53734.4.1-2010); Taber abrasion resistance (CS10/1000 g/1000 rev.) no more than 70 mg; cross-cut adhesion grade 1; density 1.15 ± 0.05 kg/dm³; non-volatile content in comp. A at least 96 %; pot life +10 °C ~40 min, +20 °C ~25 min, +30 °C ~12 min; service temperature from −10 to +60 °C; class KM2
Consumption80–100 g/m² per coat (no more than three coats); in the system, main layer 0.3 kg/m² in three passes
Shelf life6 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2312-055-94613022-2016; fire safety KM2 (G1, V2, T2, D1, RP1), certificate of conformity; test methods GOST R 53734.4.1-2010, GOST 28513-90, GOST R 52487-2005, GOST 15140, GOST 11529-86 (section 3) / GOST 32017-12

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.