LEVL (INGRI)

LEVL Coat 308 — economical filled epoxy self-levelling floor

Epoxy floors

The economical version of the epoxy self-levelling floor, LEVL Coat 308, is never used without mineral filler: quartz sand is added to the mix at a ratio of 1 : 0.5, up to 1 : 1 permitted. The result is filled and highly filled, smooth or textured coatings; laying is carried out at temperatures from +15 to +30 °C over LEVL Coat epoxy primers. Compressive strength is at least 55 MPa, flexural 25 MPa, Taber abrasion up to 55 mg. Applications: offices, retail, healthcare, warehouses, workshops, garages, car parks and rooms with a “wet cycle”.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Useretail and public buildings, food and pharmaceutical, chemically resistant, warehouses and logistics, production workshops, car parks and ramps, wet rooms
Baseepoxy resin (two-component composition; used only with mineral filler)
ColourRAL colours; gloss finish (RAL 7043 and 5001 are non-standard)
Packagingkit of 2.4 and 25 kg; A : B = 3.76 : 1.00 (LEVL Coat 308) / 3.17 : 1.00 (LEVL Coat 308 Color) by weight
Application methodfilled and highly filled self-levelling, smooth and textured floor coatings over LEVL Coat 101 / 102 W / 103 / 104 Rapid / 108 / 118 primer; filling with quartz sand 1.0 : 0.5 (up to 1 : 1 permitted), not to be used without filler; pouring, squeegee/notched trowel, spiked roller; textured: broadcast to excess and a finishing coat
Application temperatureair and substrate +15…+30 °C (recommended +17…+23 °C); material +15…+25 °C; air humidity no more than 80 %; substrate moisture no more than 5 % (primers 101/103/104 Rapid/108/118) or 10 % (102 W); 3 °C above the dew point
Curinglight loads / recoat interval: +15 °C ~32 h, +23 °C ~16 h, +30 °C ~12 h; foot traffic: ~6 / ~3 / ~2 days; full strength gain: ~10 / ~7 / ~5 days; next coat after 16–48 h at 23 °C
Key propertiesShore D hardness (7 days) at least 70 (308) / 65 (308 Color); ultimate compressive strength (7 days) at least 55 MPa; flexural at least 25 MPa; tensile strength at break at least 14 / 10 MPa; adhesion to concrete (with LEVL Coat 101 primer) at least 2.5 MPa (failure in the concrete); Taber abrasion (CS10 / 1000 g / 1000 rev.) no more than 55 mg; density 1.40 ± 0.05 / 1.35 ± 0.05 g/cm³; non-volatile content at least 96 %; pot life +15 °C ~45 min, +20 °C ~30 min, +30 °C ~15 min; service temperature from −10 to +60 °C (highly filled: short-term up to +90 °C); chemical resistance: on request
Layer thicknessself-levelling filled (+50 % sand) 1.5–5.0 mm; highly filled 3–12 mm
Consumptionsmooth filled 2 mm: LEVL Coat 308 2.20 kg/m² + quartz sand 0.1–0.3 mm 1.10 kg/m²; textured highly filled 6 mm: 2.94 kg/m² + filler sand 0.1–0.3 mm 1.98 kg/m² + broadcast 0.3–0.9 mm 9.24 kg/m² + finishing coat 0.70 kg/m²; theoretically per 1 mm of filled material (1.0 : 0.5): 308 — 1.65 kg/m², 308 Color — 1.67 kg/m²
Shelf life12 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-006-94613022-2006; works per SP 29.13330.2011 and SP 71.13330.2017; test methods GOST 31992.1, GOST R 31939, GOST 24621, GOST 11262, GOST 28574

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.