PLAMCOR-1 water-based fire-retardant paint for steel structures (VMP)

Fire protection of steel structures

PLAMCOR-1 is a water-based intumescent paint on a vinyl acetate dispersion that protects steel structures of buildings and equipment against fire; its fire protection performance is 45, 60 and 90 minutes. Per GOST 15150 the coating is designed for placement categories 3 and 4 at air humidity up to 85 %; it is not moisture-resistant, so moisture and condensation are excluded. The paint is thinned with water and applied at +5 to +40 °C over TSINEP, IZOLEP or VINIKOR primers, and if necessary it is topcoated with POLITON-UR, VINIKOR-62 or PF-115 enamel. With primer and enamel, the coating lasts at least 18 years in category 4 and at least 10 years in category 3.

Specifications

ManufacturerVMP — AO “NPKh VMP”, Yekaterinburg
Fire protection performance45, 60 and 90 min
Applicationsteel structures
Service conditionsindustrial, civil and public buildings and equipment; macroclimatic regions UKhL and KhL, atmosphere types I and II, placement categories 3 and 4 per GOST 15150, relative air humidity no more than 85 %; the coating is not moisture-resistant — exposure to moisture, incl. condensation, must be excluded during application and service; service life as part of a complex coating with primer and topcoat enamel — at least 18 years (placement category 4), at least 10 years (placement category 3)
Basewater-based vinyl acetate dispersion with gas-forming and foam-forming fillers, pigments and functional additives; intumescent, intumescence ratio at least 10; non-volatile content by mass 65–69 %, by volume — 55 %
Colourwhite, shade not standardised; uniform coating
Packagingplastic buckets 20 l, cans 1 l
Application methodairless spray (nozzle 0.019–0.021″, pressure at least 20 MPa), brush, roller; if necessary, thin with water up to 10 % by mass; equipment cleaning — with water
Application temperaturefrom +5 to +40 °C, relative humidity up to 85 %; application at above-zero temperatures and in heated premises
Dryingto degree 3 per GOST 19007 — no more than 4 h at (20±2) °C; interval between coats — at least 12 h; before the topcoat enamel — at least 24 h; full drying — at least 3 days; natural drying
Compatible primers and topcoatsused as the top or intermediate fire-protective coating in complex systems protecting against corrosion and fire; primers TSINEP, IZOLEP-primer, IZOLEP-mastic, VINIKOR-ecoprime-01, VINIKOR-061, VINIKOR primer-enamel, GF-021 — the paint is applied no earlier than 24 h after priming; topcoat enamels POLITON-UR (UV), POLITON-UR, VINIKOR-62, EVOPOL-12 primer-enamel, PF-115; primers and enamels of other manufacturers — subject to approval by VMP
Shelf life12 months from the date of manufacture in tightly closed containers; storage and transport per GOST 9980.5-2009 at temperatures from +5 to +40 °C, protected from precipitation and direct sunlight
StandardsTU 20.30.11-082-12288779-2021 (replacing TU 2316-082-12288779-2011); GOST 15150; GOST 9980.5-2009; GOST 19007; certificate of conformity under TR EAEU 043/2017; NSOPB certificate; state registration certificate; MGSU conclusion on seismic resistance; the manufacturer’s QMS is certified to ISO 9001

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.