LEVL Coat 502 — clear epoxy layer for self-levelling 3D floors
LEVL (INGRI)

LEVL Coat 502 — clear epoxy layer for self-levelling 3D floors

Epoxy floors

A self-levelling 3D floor is built like this: decorative PVC film or fabric is laid on a LEVL Coat 307 base, primed with LEVL Coat 551 and covered with a clear layer of LEVL Coat 502. The three-component epoxy compound is spread with a squeegee or notched trowel and rolled with a spiked roller, optionally coated with LEVL Coat 254 matt varnish. Taber abrasion is up to 50 mg, Shore D hardness from 55, elongation at break at least 35 %, class KM2. Work is carried out at +15…+30 °C; dust and cold cause surface defects.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Usedecorative
Baseepoxy resin, reactive diluent, functional additives, polyamine hardener; three-component, clear
Colourclear gloss coating (matt varnish optional)
Packagingkit (A+B1+B2) 20 kg: A — 20 l pail of 13.2 kg; B1 — 10 l jerrycan of 6 kg; B2 — 1 l can of 0.8 kg; A : B1 : B2 = 2.2 : 1 : 0.13 (by weight)
Application methodclear protective layer of a 3D floor on polymer and mineral surfaces: LEVL Coat 307 base, decorative PVC film (or fabric), LEVL Coat 551 PVC primer, then LEVL Coat 502 by squeegee/notched trowel with spiked-roller rolling; optionally LEVL Coat 254 matt varnish; add B2 15 min after B1
Application temperatureair +15…+30 °C (recommended +20…+25 °C); substrate +15…+30 °C; material +15…+30 °C (recommended +15…+25 °C); air humidity up to 80 %; substrate moisture: not applicable (laid on a polymer base); 3 °C above the dew point
Curinglight loads: +15 °C 48 h, +20 °C 36 h, +30 °C 24 h; foot traffic: 6 / 4 / 2 days; full loads: 10 / 7 / 5 days; varnish no earlier than 48 h at 20 °C
Key propertiesTaber abrasion no more than 50 mg; Shore D hardness (7 days) at least 55; relative elongation at break at least 35 %; ultimate strength at maximum load 7.5 MPa; density 1.06 ± 0.05 g/cm³; non-volatile content at least 99 %; chemical resistance; pot life +15 °C 60 min, +20 °C 50 min, +30 °C 20 min; service temperature from −10 to +60 °C; class KM2
Layer thicknesscoating thickness 1.5–3 mm (3D-floor finishing layer, design value 2.0 mm)
Consumptionfinishing layer 2.0 mm: LEVL Coat 502 2.2 kg/m²; in the system: LEVL Coat 307 base 1.5 kg/m² + sand 1.0 kg/m², LEVL Coat 551 PVC primer 0.1 kg/m², LEVL Coat 254 matt varnish 0.08 kg/m² (optional)
Shelf life6 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-006-94613022-06 with Amendment No. 1; fire safety KM2 (V2, T1, D2, RP1), No. 123-FZ; test methods GOST 31992.1, GOST R 31939, GOST 24621, GOST 11262

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.