Monopol Policrete 610 — high-build polyurethane-cement floor
Monopol

Monopol Policrete 610 — high-build polyurethane-cement floor

Polyurethane-cement floors

The high-build Policrete 610 is designed for moderate and significant loads in dry and wet conditions. It is used in the food and processing industry, at chemical plants, in cold stores and freezer rooms, car parks, warehouses, workshops, the power sector and pharmaceuticals. Compressive strength at least 57 MPa, flexural strength at least 16.9 MPa, slip resistance R10, class KM1, water absorption 0%. The coating is resistant to water, oils, petrol, solvents, dilute acids and alkalis.

Specifications

ManufacturerMonopol — OOO “TEKHBETON”
Typepolyurethane-cement floors
Usefood and pharmaceutical, chemically resistant, car parks and ramps, warehouses and logistics, production workshops, wet premises
Basepolyurethane resin with mineral filler and pigment paste, four-component high-build
Colouraccording to the colour chart
Packaging30.3 kg: component A 2.5 kg + B 2.8 kg + C 25 kg (bag) + pigment paste 150 ml
Application methodhigh-build self-levelling layer 6-10 mm over Monopol Policrete 100 primer
Application temperaturesubstrate temperature at the time of application from +10 °C to +25 °C; recommended air humidity from 35% to 75%
CuringAt +20 °C: walking after 12 hours; light vehicle loads after 24 hours; full vehicle loads and chemically aggressive liquids after two days
Key propertiesCompressive strength at least 57 MPa; flexural strength at least 16.9 MPa; impact strength 4.2 J/cm²; abrasion no more than 0.11 g/cm²; AR 0.5; Shore D at least 81; R10; water absorption 0%; KM1; vapour permeability yes; density 2.23 g/cm³; adhesion > 4.5 MPa (cohesive failure in concrete); chemical resistance to water, dilute and medium-concentration alkalis and acids, oils, petrol, solvents
Layer thicknessfrom 6 to 10 mm
Consumptionfrom 2.3 kg/m² per 1 mm of layer thickness
Shelf life12 months from the date of manufacture; store at a temperature not below +5 °C and not above +30 °C
Standardsfire hazard class KM1

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.