QTP® 1751 — fast-curing epoxy paint
QTP

QTP® 1751 — fast-curing epoxy paint

Epoxy floors

This epoxy compound is used over QTP 1700 primer to produce a thin-film paint and slip-resistant finish for rapid floor repairs. Work is permitted at substrate and air temperatures from +5 °C. At +20 °C, pedestrian traffic is allowed after 3 h and full mechanical load after 4 h. Shore D hardness is 87–93; pot life is 17 minutes.

Specifications

ManufacturerQTP — OOO “KTP”, Noginsk
Typeepoxy floors
Useproduction workshops, warehouses and logistics, car parks and ramps
Basetwo-component fast-curing epoxy paint compound, solvent-free
Colourtintable
Packaging20.8 kg kit: component A 16 kg (20 l pail) + component B 4.8 kg (5 l pail)
Application methodrapid floor repair; thin-film paint and slip-resistant finish coat (QTP 1700 primer)
Application temperaturesubstrate and air +5…+30 °C
Curingat 0/+10/+20/+30 °C: pedestrian traffic after 4 / 3.5 / 3.0 / 2 h; passenger car traffic after 6 / 4 / 3 / 2.5 h; full mechanical load after 12 / 8 / 4 / 3 h; full chemical load after 4 / 3 / 2 days / 24 h
Key propertiescompressive strength 79 MPa; flexural strength 18 MPa; tensile strength 24 MPa; Shore D hardness 87–93; Taber abrasion 57 mg; heat resistance: continuous +70 °C, up to 7 days +80 °C, up to 12 h +100 °C; pot life 17 min
Consumptionon concrete: QTP 1700 primer 0.25–0.35 + 1st coat 0.25–0.35 + 2nd coat 0.15–0.25 kg/m2; on anti-slip coatings: 0.75 + 0.35 kg/m2
Shelf life12 months from the date of manufacture in unopened containers, in a dry, cool room at +15…+25 °C, protected from sub-zero temperatures and direct sunlight
StandardsSGR KG.11.01.09.008.E.002319.06.18 dated 19.06.2018 (epoxy enamels, TU 2312-003-28912903-2014; grade listed); test methods DIN / EN ISO / Taber

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.