WETISOL I-5020 — injection resin with rigid foam
Wetisol (INGRI)

WETISOL I-5020 — injection resin with rigid foam

Injection waterproofing

On entering water, WETISOL I-5020 foams and hardens, forming a rigid foam. The solvent-free resin is designed to stop pressurised water, including sea water, at pressures of up to 0.5 atm, to pre-seal water-bearing cracks, fill voids and bind soil. Foaming starts after 7–13 s, the foam rises in 70–90 s, and the reaction rate is controlled by the catalyst. After the leak is stopped, the crack is sealed with WETISOL I-5106 LV.

Specifications

ManufacturerWetisol (INGRI) — OOO “Ingri”
Typeinjection waterproofing
Useleak repair, foundations and basements
Basewater-reactive polyurethane injection resin (comp. A) with catalyst (comp. B), solvent-free; foams on contact with water, forming a rigid foam
Colourcomp. A — transparent brownish liquid; comp. B — transparent liquid, colourless to yellowish
Packagingkit A+B 10 kg: comp. A 9.09 kg (metal bucket), comp. B 0.91 kg (plastic bottle)
Application methodstopping the ingress of pressurised water (including sea water) with pressure up to 0.5 atm; preliminary sealing of water-bearing cracks; filling and sealing of small and especially large volumes and voids; stopping small and medium water inflows followed by injection of WETISOL I-5106 LV; strengthening and binding of soil; at water pressure above 0.5–1 atm — WETISOL I-5137; if there is not enough water in the zone — preliminary or subsequent water injection; one-component pump with hose, packer nozzle and pressure gauge; injection points 50–60 mm from the crack, one on each side, spacing max 200 mm (for membranes — up to +100 mm); holes Ø12 mm (minor repairs) – 30–40 mm (membrane) at 40–50°, depth up to 450–500 mm (for a membrane 600–800 mm); plastic packers up to Ø18 mm; lay injection hoses where possible (mandatory when repairing foundation waterproofing and strengthening soils); A:B = 1:(0.06–0.1) by weight, scales ±1%, mix until homogeneous; before use keep for at least 12 h at +15…+30 °C; cleaning with WETISOL S-Clean, hardened material — mechanically
Application temperaturestructure, water and air +5…+30 °C
Curingstart of foaming 7–13 s, foam rise 70–90 s (at 23 °C, A:B:water = 10:1:0.5)
Key propertiesdynamic viscosity at 23 °C: comp. A 600±100 mPa·s, comp. B 30±10 mPa·s (GOST 25271); density at 23 °C: comp. A 1.15±0.05 g/cm³, comp. B 1.0±0.05 g/cm³ (GOST 31992.1); foaming start time 7–13 s, foam rise time 70–90 s (per the TU method); forms a rigid foam; the reaction rate is controlled by the catalyst; service temperature of the cured material from −10 to +50 °C
Shelf life12 months from the date of manufacture in closed undamaged original containers at +10…+30 °C; reacts with air moisture (a film forms in an open container)
StandardsTU 2257-008-94613022-13 with amendment No. 1; fire safety — not subject to certification

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.

Other materials by Wetisol (INGRI)

Wetisol (INGRI)

Wetisol S-CP — epoxy primer for polyurea

Two-component epoxy primer for concrete and brick under Wetisol Spray sprayed polyurea; adhesion to concrete over 4.0 MPa.

Price on request