REKS® Fab-10P — fibre-reinforced concrete mix with crushed granite for pavement repair
REKS

REKS® Fab-10P — fibre-reinforced concrete mix with crushed granite for pavement repair

Flowable repair mortars

REKS® Fab-10P is a fibre-reinforced non-shrink cementitious concrete mix supplied as a 35 kg kit: a 25 kg bag of dry mix and a 10 kg pail of crushed granite. It is used to repair airfield and road pavements with partial or full slab replacement, industrial floors and shopping-centre floors, bridge piers, beams and slabs, and for monolithic grouting of joints in precast reinforced concrete. Class R4 per GOST R 56378, aggregate size 10 mm, compressive strength at least 30 MPa after one day and 65 MPa after 28 days, freeze-thaw resistance F2 400.

Specifications

ManufacturerREKS — OOO “SPS”
Typeflowable repair mortars
Useroads and airfields, floors, bridges and overpasses, hydraulic structures and dams, tanks and treatment plants
Basefibre-reinforced non-shrink cementitious concrete mix
Colourgrey
Packagingkit 35 kg; component 1: dry mix, bag 25 kg; component 2: crushed granite, plastic pail 10 kg
Application methodrepair of airfield and road pavements with partial or full replacement of pavement slabs; repair of concrete and reinforced concrete structural elements, including sloped bases; repair of reinforced concrete bridge piers, beams and deck slabs working under static and moderate dynamic loads; monolithic grouting of joints in precast reinforced concrete structures (piers, concrete slabs, etc.); repair of hydraulic structures
Application temperaturenot below +5 °C
Curingprotection from precipitation for at least 24 h; in hot and windy weather — water spraying and covering with film
Key propertiesmodulus of elasticity: ≥25,000 MPa; density of hardened mortar: 2.4 ± 5 % t/m³; freeze-thaw resistance: F2 400; bond to substrate at 28 days: ≥2.0 MPa; water impermeability: W16; compressive strength at 28 days: ≥65 MPa; flexural strength at 1 day: ≥5 MPa; flexural strength at 28 days: ≥7 MPa; bond to substrate at 28 days after 50 freeze-thaw cycles in salts: ≥2.0 MPa; aggregate size: 10 mm; flowability retention: 30 minutes; compressive strength at 1 day: ≥30 MPa; flowability (concrete flow trough): 30–60 seconds; capillary water absorption: no more than 0.4 kg/(m²·min⁰·⁵); sulphate resistance coefficient (365 days): 0.982 %
Shelf life12 months from the date of manufacture
Standardsclass R4 per GOST R 56378

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.