LEVELINE FC807 non-sparking dry-shake topping — for explosion and fire hazard sites
INDASTRO

LEVELINE FC807 non-sparking dry-shake topping — for explosion and fire hazard sites

Toppings

The non-sparking filler is the main difference between FC807 and other LEVELINE toppings: the surface does not spark under impact, so the mix is used at sites with explosion and fire safety requirements. The technology is the usual one for a dry-shake topping — application onto fresh concrete and floating, and the manufacturer recommends the non-sparking screed FC806 as the base. Compressive strength at 28 days is at least 70 MPa, abrasion class AR1, service from −60 to +200 °C.

Specifications

ManufacturerINDASTRO — OOO “Sedrus”
Typetoppings
Useproduction workshops, warehouses and logistics
BasePortland cement, non-sparking mineral filler, modifying additives
Colourgrey
Packaging25 kg bags: paper (Kolomna, Berdsk, 60 per pallet), plastic (Ulyanovsk 54; Nevinnomyssk 56 per pallet)
Application methoddry application onto freshly laid concrete ~2/3 + ~1/3, floating with a power trowel, finishing; LEVELINE SP2 impregnation; joint cutting within 24 hours; the non-sparking screed FC806 is recommended beforehand
Application temperature+10…+30 °C
Curingfoot traffic ~ 24 hours
Key propertiesDoes not produce sparks under impact; abrasion EN 13892-4 (BCA) AR1; impact at least 15 kg from a height of 1 m; compressive strength at 24 h at least 15 MPa, at 28 days at least 70 MPa; flexural strength at least 7 MPa; bond at least 2 MPa; aggregate size no more than 3 mm; service temperature -60…+200 °C
Layer thickness3-4 mm
Consumption3-6 kg/m2
Shelf life12 months (paper packaging); 24 months (plastic)
Standardsmanufacturer's TU; EN 13892-4 (BCA), GOST 30353

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.