Izhora MBP-G/Shm-75 joint mastic is a hot bitumen-polymer compound for road pavements: it is poured into joints and cracks, and into junctions of the pavement with tram rails and barrier structures. Cracks are first routed with a milling cutter, cleaned, dried and primed, then the mastic, heated in a kettle with indirect heating, is poured with a joint-filling machine or pouring can. Surface waterproofing is also permitted — by brush or by pouring and spreading with a rubber squeegee. Elasticity at +25 °C is 90 %, the softening point is 90 °C, and the material is not intended for expansion joints.
| Manufacturer | Rastro (LAKHTA, SLAVYANKA, Izhora) — ZAO “Rastro” |
|---|---|
| Type | joint sealants |
| Use | joints and junctions |
| Base | one-component hot-applied bitumen-polymer mastic (bitumen, plasticisers, filler, polymer additives) |
| Colour | black |
| Packaging | 24 kg cardboard drums with polyethylene film or 25 kg cardboard boxes with release film |
| Application method | remove loose pieces and, if necessary, old sealant; rout cracks with a milling cutter to a filling width of 8…40 mm; clean with a disc brush and compressed air, dry, at low temperatures (down to −10 °C) heat with a torch; prime (Izhora NP-02 recommended); heat in automatic kettles with indirect heating and agitation (direct heating is prohibited); pour only onto dry primed surfaces with a joint-filling machine or pouring cans to a level 3–5 mm below the pavement; for waterproofing — by brush or by pouring and spreading with a rubber squeegee |
| Application temperature | air not lower than −10 °C |
| Curing | traffic is opened after the mastic has cooled to air temperature and no longer sticks to wheels |
| Key properties | softening point (ring and ball) 90 °C; needle penetration at +25 °C 40 (0.1 mm); ductility at +25 °C 70 cm; elasticity at +25 °C 90 %; bond strength to concrete 0.7 MPa, to steel 1.2 MPa; flexibility on a Ø10 mm rod at −15±1 °C — no cracks; water absorption over 24 h 0.2 %; water-tightness at 0.03 MPa for 10 min — no wet spot; chemical resistance (3 % salt, 3 % NaOH) — resistant; density 1.15 kg/dm3; all climatic zones; not for expansion joints |
| Consumption | 2.1 kg/linear m per 30 × 60 mm joint; 2.3 kg/m² for surface waterproofing with a 2 mm coat |
| Shelf life | 24 months from the date of manufacture |
| Standards | TU 5775-010-11149403-2004 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Winter two-component polyurethane sealant for reinforced concrete and facade joints; applied at air temperatures from −20 to +15 °C.
Mastic based on divinyl-styrene and acrylic polymers for foundations, roofs, bridges and tanks; bond to concrete and metal 2.0 MPa.
Penetrating cement mix for foundations, basements and tanks that raises the water-tightness grade of concrete by 4…6 steps.
Bitumen-polymer mastic for protecting pipelines, tanks and underground structures from moisture, soil corrosion and stray currents.
Cement plaster that levels and waterproofs concrete, reinforced concrete and brick at the same time; mortar grade W16.
Solvent-based bitumen-polymer mastic for external waterproofing of foundations, piles and tanks; applied at air temperatures from −10 °C.