LEVL Coat 171 — methyl methacrylate primer for MMA systems
LEVL (INGRI)

LEVL Coat 171 — methyl methacrylate primer for MMA systems

Methyl methacrylate floors

The LEVL methyl methacrylate system starts with LEVL Coat 171 carboacrylate resin primer, followed by the LEVL Coat 573 main layer and the LEVL Coat 271 finish. The primer is applied by roller onto concrete or a cement-sand screed and immediately broadcast with quartz sand; the next layer can be laid after about an hour at +20 °C. Work is also possible in frost, down to −10 °C, with LEVL Coat 075 accelerator; supply and exhaust ventilation is required. Adhesion to the substrate is at least 2.5 MPa, service from −30 to +60 °C.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typemethyl methacrylate (MMA) floors
Useoutdoor areas
Basecarboacrylate (MMA) resin; component B: LEVL Coat 070 catalyst, at sub-zero temperatures LEVL Coat 075 accelerator
Colourclear, colourless to light brown
Packaging1 kg metal can; 10 kg and 20 kg metal pails; LEVL Coat 070 catalyst depending on temperature: −10 °C 4 % (+ accelerator 2 %), 0 °C 3 % (+2 %), +10 °C 3 %, +15 °C 2 %, +20 °C 1 %, +30 °C 1 % (by weight)
Application methodprimer for concrete substrates and cement-sand screeds (normal and absorbent) under all LEVL Coat carboacrylate systems (573 + 271): by roller with an immediate broadcast of quartz sand; next coat after approx. 1 h at 20 °C (2 % catalyst)
Application temperatureair and substrate from minus 10 °C to +25 °C; material +5…+25 °C (optimum +17…+23 °C); air humidity no more than 80 %; substrate moisture no more than 5.0 % by weight; 3 °C above the dew point; below 0 °C, with LEVL Coat 075 accelerator; supply and exhaust ventilation required
Curingfoot traffic: −10 °C ~24 h, 0 °C ~12 h, +10 °C ~6 h, +20 °C ~4 h, +30 °C ~2 h; light loads: ~48 / ~48 / ~12 / ~12 / ~6 h; full strength gain: ~4 / ~3 / ~2 / ~1 days / ~12 h; pot life ~5–25 min, curing ~10–60 min depending on temperature
Key propertiesAdhesion to substrate at least 2.5 MPa; density 1.00 ± 0.05 g/cm³; non-volatile content at least 98 %; resistance to bacteriological attack; fast curing; application at sub-zero temperatures; service temperature from minus 30 °C to +60 °C, short-term up to +90 °C
Layer thickness0.4–0.5 mm
Consumption0.4–0.5 kg/m² per coat (not below 0.4 kg/m², otherwise polymerisation may not start); in the system: LEVL Coat 171 0.4 kg/m² + LEVL Coat 070 0.008 kg/m² + quartz sand 0.4–0.8 mm (0.8–1.2 mm) 1.0 kg/m²
Shelf life6 months from the date of manufacture (in unopened packaging); recommended storage temperature +15…+25 °C
StandardsTU 2312-037-94613022-15; test methods GOST 31992.1, GOST 31939, GOST 28574

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.