LEVL Coat 306 DA — decontaminable epoxy self-levelling floor
LEVL (INGRI)

LEVL Coat 306 DA — decontaminable epoxy self-levelling floor

Epoxy floors

LEVL Coat 306 DA is intended for nuclear industry rooms subject to decontamination: a smooth seamless self-levelling floor on epoxy resin without organic solvents or plasticisers. The compound is poured over a primed substrate, spread with a squeegee or notched trowel and rolled with a plastic spiked roller; it must not be thinned with solvents. Shore D hardness is at least 70, Taber abrasion up to 55 mg, elongation at break from 10 %, adhesion to concrete 2.5 MPa. Colour to the RAL chart, gloss surface.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Useproduction workshops
Baseepoxy resin; no organic solvents or plasticisers
ColourRAL colours; uniform gloss finish
Packaging25 kg kits (A and B in two containers); A : B = 3.35 : 1 (by weight)
Application methodsmooth seamless decontaminable self-levelling floor coating for rooms subject to decontamination at nuclear industry facilities; poured over a primed substrate (LEVL Coat 101/108/118 or 102 W primer), squeegee or notched trowel, rolling with a plastic spiked roller; thinning with solvents is not permitted
Application temperatureair +10…+30 °C (recommended +17…+23 °C); substrate +10…+30 °C (recommended +17…+25 °C); material +15…+25 °C; air humidity up to 80 %; substrate moisture no more than 5 % (primers 101/108/118) or no more than 10 % (102 W); 3 °C above the dew point
Curinglight loads: +10 °C 32 h, +20 °C 16 h, +30 °C 12 h; foot traffic: 6 / 3 / 2 days; full strength gain: 10 / 7 / 5 days; next coat after 12–48 h at 20 °C
Key propertiesDecontaminable coating; Shore D hardness (7 days) at least 70 (in bright colours possibly down to 65); Taber abrasion (CS10 / 1000 g / 1000 rev.) no more than 55 mg; adhesion to concrete (with LEVL Coat 101 primer) at least 2.5 MPa; elongation at break at least 10 %; tensile strength at break at least 10 MPa; density 1.35 ± 0.05 g/cm³; non-volatile content at least 96 %; pot life +10 °C 60 min, +23 °C 30 min, +30 °C 15 min; service temperature from −10 to +60 °C; chemical resistance: on request
Layer thicknesswearing / coloured layer from 2 to 5 mm
Consumptionmain layer 2 mm: 2.7 kg/m²; theoretical consumption 1.35 kg/m² per 1 mm of thickness
Shelf life12 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-006-94613022-06; works per SP 29.13330.2011 and SP 71.13330.2017 (Table 8.12); test methods GOST 31992.1, GOST R 31939, GOST 28574, GOST 24621, GOST 11262

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.