REKS® EPO INZH — low-viscosity epoxy for injecting cracks in concrete
REKS

REKS® EPO INZH — low-viscosity epoxy for injecting cracks in concrete

Crack injection resins

Injection of cracks and pores in concrete to restore load-bearing capacity, including where erosion is severe, is carried out with REKS® EPO INZH. The two-component low-viscosity amber epoxy protects and strengthens load-bearing concrete structures and brick masonry; the viscosity of the mixed components is no more than 400 cP, and the gel time is from 30 minutes. After 7 days compressive strength is at least 70 MPa, tensile strength from 25 MPa, adhesion to steel at least 6 MPa; 5 and 10 kg kits in metal containers.

Specifications

ManufacturerREKS — OOO “SPS”
Typecrack injection resins
Usecolumns and beams, industrial buildings
Basetwo-component low-viscosity epoxy injection resin
Colouramber
Packagingkit 5 kg (A 4 kg + B 1 kg) or 10 kg (A 8 kg + B 2 kg), metal containers
Application methodprotection and strengthening of load-bearing concrete structures, brick masonry, etc.
Application temperaturecomponents at about +20 °C before use
Curingfull readiness for service ≤7 days
Key propertiestensile strength at 7 days: ≥25 MPa; adhesion to concrete: exceeds the cohesion of concrete; compressive strength at 7 days: ≥70 MPa; elongation at break: ≥10 %; viscosity of component A: ≤350 cP; viscosity of component B: ≤500 cP; gel time: ≥30 minutes; full readiness for service: ≤7 days; water absorption: at 1 day ≤0.4 %; adhesion to steel: ≥6 MPa; viscosity of the mixed components A and B: ≤400 cP
Shelf life12 months from the date of manufacture; storage at +10…+25 °C

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.