TAIKOR Floor 710 by TECHNONICOL is a low-viscosity two-component epoxy compound that produces a uniform gloss coating in any RAL colour. It is used in healthcare, offices, food, chemical and pharmaceutical production workshops, warehouses, car parks, cleanrooms, schools and children’s facilities. Abrasion no more than 49 mg, Shore D hardness about 80, adhesion to concrete from 2 MPa, service from −20 to +50 °C. The coating is resistant to water, petroleum products, salts, dilute acids and alkalis.
| Manufacturer | TAIKOR (TECHNONICOL) — OOO “TECHNONICOL – Construction Systems” |
|---|---|
| Type | epoxy floors |
| Use | production workshops, warehouses and logistics, car parks and ramps, food and pharmaceutical, retail and public, chemically resistant |
| Base | low-viscosity two-component epoxy self-levelling compound; non-volatiles at least 98 % (in the system — 'solvent-free') |
| Colour | tinted to any colour from the RAL catalogue; uniform gloss |
| Packaging | pails 5 and 20 l; net weight 5; 20 kg (kit A+B) |
| Application method | over primed concrete/cement screed (TAIKOR Primer 160 primer recommended); concrete cured for 28 days, screed moisture no more than 4 wt. %, substrate compressive strength at least 20 MPa, pull-off strength at least 1.5 MPa; A:B = 100:25 by weight, mix the whole kit with a mixer at 150-300 rpm; pour, spread with a trowel/gauge rake/roller, roll with a spiked roller; working time on the floor about 40 min at +20 °C; addition/broadcasting of calcined quartz sand is permitted |
| Application temperature | air +5…+25 °C, relative humidity no more than 80 %; substrate from +8 to +25 °C; surface 3 °C above the dew point |
| Curing | drying to degree 3 at +20 °C no more than 6 h; recoat window 12-72 h; full cure 7 days; of the TN-POL NALIVNOY Epoxy system: walking after 36/24/18 h, light load 5/3/2 days, full load 10/7/5 days at +10/+20/+30 °C |
| Key properties | Abrasion (CS10 wheel, 1000 cycles, ASTM D 4060) no more than 49 mg; tensile strength at least 30 MPa; elongation at break at least 4 %; Shore D hardness about 80; adhesion to concrete at least 2 MPa; service temperature -20…+50 °C; density after mixing 1.45-1.55 g/cm3; pot life at least 40 min; resistance to water, petroleum products, salts, dilute alkalis and acids; in the TN-POL NALIVNOY Epoxy system: RP1, V2, D2, T2, non-sparking — yes |
| Layer thickness | in the TN-POL NALIVNOY Epoxy system 1.50-2.00 mm |
| Consumption | theoretical consumption at a 2 mm layer — 3 kg/m2; in the system 2.250-3.000 kg/m2 |
| Shelf life | 12 months; storage +5…+25 °C; transport -30…+30 °C (after frost keep warm for 24 h) |
| Standards | TU 20.30.22-143-72746455-2023; HS code (TN VED) 3214 90 0009; methods ASTM D 4060, GOST 34370, GOST 24621, GOST 28574 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Epoxy self-levelling floor system based on TAIKOR Primer 160 and Floor 710 for sales floors, medicine, schools, car parks, warehouses and food workshops.
Elastic polyurethane self-levelling compound without a strong odour for workshops, warehouses, car parks and public buildings; elongation at break from 10%.
Coloured thin-layer floor of TAIKOR Primer 150 primer-enamel and Top 425 enamel for production premises with dry and wet processes.
Antistatic polyurethane self-levelling floor for explosion-hazard production, electronics, laboratories, car services and filling stations; no more than 10⁶ Ω.
Antistatic polyurethane floor system with copper tape and TAIKOR Floor 720 AS for explosion-hazard production, electronics and filling stations; up to 10⁶ Ω.
Light- and weather-resistant polyurethane enamel for thin-layer floors in car parks, warehouses, stands and outdoor areas; winter version applied down to −10 °C.