TN-POL NALIVNOY Epoxy is a ready-made three-layer system: TAIKOR Primer 160 primer, a broadcast of calcined quartz sand and a TAIKOR Floor 710 self-levelling layer. The manufacturer offers thin-layer, smooth, filled, non-slip and reinforced versions for medium and heavy wearing loads with chemical exposure. The coating is non-sparking, solvent-free and impermeable to liquids; fire performance — RP1, V2, D2, T2. At +20 °C foot traffic is possible after 24 hours, full load after 7 days.
| Manufacturer | TAIKOR (TECHNONICOL) — OOO “TECHNONICOL – Construction Systems” |
|---|---|
| Type | floor material |
| Use | retail and public, car parks and ramps, wet premises, warehouses and logistics, production workshops, food and pharmaceutical, chemically resistant |
| Base | epoxy self-levelling floor: TAIKOR Primer 160 + quartz sand + TAIKOR Floor 710 |
| Colour | tinted to the RAL catalogue; uniform gloss coating |
| Application method | TAIKOR Primer 160 primer, broadcast of calcined quartz sand 0.4-0.8 / 0.5-1.0 / 0.8-1.2 mm onto the tacky primer, removal of loose sand, pouring of TAIKOR Floor 710 with a gauge rake/notched trowel, rolling with a spiked roller after 5-7 min; substrate: compressive strength at least 20 MPa, pull-off at least 1.5 MPa, moisture no more than 4 %; versions: thin-layer, smooth, filled, non-slip, reinforced |
| Application temperature | air and substrate from +8 to +25 °C |
| Curing | walking after 36/24/18 h; light load 5/3/2 days; full load 10/7/5 days (at +10/+20/+30 °C) |
| Key properties | Service temperature -20…+50 °C; flame spread RP1; ignitability V2; smoke generation D2; toxicity T2; non-sparking — yes; high mechanical and chemical resistance, impermeable to liquids, solvent-free, non-slip finish possible |
| Layer thickness | main layer 1.50-2.00 mm; versions: thin-layer (paint) 0.4-0.5 mm, smooth 1.5-2.0 mm, filled 1.5-3.0 mm, non-slip 2.0-2.5 mm, reinforced 3.0-4.5 mm; actual from 0.5 to 5 mm |
| Consumption | TAIKOR Floor 710 2.250-3.000 kg/m2; quartz sand 0.500-1.000 kg/m2 (in excess up to 2.5 kg/m2); TAIKOR Primer 160 0.300-0.500 kg/m2 |
| Standards | GOST R 51032-97, GOST 30402-96, GOST 12.1.044-2018, STO 004-02495342-2010 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Antistatic polyurethane self-levelling floor for explosion-hazard production, electronics, laboratories, car services and filling stations; no more than 10⁶ Ω.
One-component matt primer-enamel for economical painting of concrete floors with light and moderate loads, as well as metal; application from −30 °C.
Epoxy self-levelling compound for floors in workshops, warehouses, car parks, medical, food and children's facilities; abrasion to ASTM D 4060 up to 49 mg.
Epoxy primer without a strong odour for TAIKOR Floor self-levelling floors and a binder for repair compounds; adhesion to concrete from 2 MPa.
Light- and weather-resistant polyurethane enamel for thin-layer floors in car parks, warehouses, stands and outdoor areas; winter version applied down to −10 °C.
Coloured thin-layer floor of TAIKOR Primer 150 primer-enamel and Top 425 enamel for production premises with dry and wet processes.