The water-based primer on an acrylic dispersion prepares a concrete substrate for cement and polymer-cement coatings — self-levelling floors, screeds, repair compounds and toppings. It is applied by brush or roller onto dry, sound, dust-free concrete, indoors only, at temperatures from +5 to +35 °C. The formula with an antiseptic has an antibacterial effect, and the primer dries tack-free in 60 minutes. Packaging — 10 kg canisters.
| Manufacturer | INDASTRO — OOO “Sedrus” |
|---|---|
| Type | floor primers |
| Use | production workshops, warehouses and logistics |
| Base | polymer (acrylic) dispersion, antiseptic, water |
| Packaging | plastic canisters 10 kg, 60 per pallet |
| Application method | brush or roller onto dry, sound, dust-free concrete before cement and polymer-cement coatings (self-levelling floors, screeds, repair compounds, toppings); indoors only |
| Application temperature | substrate +5…+35 °C; application +5…+35 °C |
| Curing | tack-free drying 60 min |
| Key properties | Non-volatile content at least 12%; frost resistance in storage at least 5 cycles; antibacterial formula |
| Consumption | 0.1-0.25 kg/m2 |
| Shelf life | 12 months; storage +5…+35 °C |
| Standards | manufacturer's TU; SP 29.13330.2011, SP 71.13330.2017 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Finishing repair mortar with fibre and sand up to 0.63 mm for load-bearing, bridge and treatment structures; compressive strength from 20 MPa after one day.
Dry mix for hardening concrete floors that does not spark on impact, for workshops and warehouses with explosion-safety requirements; from 70 MPa.
Flowable R4 repair mortar with polymer fibre for work at −10…+10 °C on bridges, treatment plants and underground structures; 45 MPa at 28 days.
Ultra-rapid-hardening R4 grout for equipment, anchors and sleepers in track concrete; 10 MPa in compression after just 2 hours.
Thixotropic R3 cementitious mortar for structural repair of concrete and reinforced concrete in industrial buildings; compressive strength at 28 days from 35 MPa.
Solvent-free epoxy primer for self-levelling and decorative polymer floors, also a stand-alone impregnation; adhesion to concrete from 2.5 MPa.