LEVL Coat 208 — epoxy paint for concrete floors, walls and ceilings
LEVL (INGRI)

LEVL Coat 208 — epoxy paint for concrete floors, walls and ceilings

Epoxy floors

LEVL Coat 208 semi-gloss epoxy paint is suitable for floors, walls and ceilings indoors, from workshops and car parks to schools, kindergartens and healthcare facilities. The coating does not level the substrate but bridges fine cracks and gives an anti-slip effect. Two coats are applied by roller or brush over epoxy primer, or in self-priming mode, in which case three coats are applied. Taber abrasion is no more than 65 mg, service from −10 to +60 °C; RAL colours.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Useproduction workshops, car parks and ramps, food and pharmaceutical, retail and public buildings, warehouses and logistics, decorative
Baseepoxy resin (two-component paint)
ColourRAL colours; semi-gloss finish (RAL 1023, 2001, 3020 are non-standard)
Packagingkits of 2.4 kg, 10 kg, 25 kg (A and B in two containers); A + B = 3.76 : 1 (by weight)
Application methodthin-layer protective, decorative and wear-resistant coating for floors, walls and ceilings indoors; over LEVL Coat 101/103/108 primer (substrate moisture up to 5 %) or 102W/106M (up to 10 %); self-priming is permitted; velour roller or brush, 2 coats (3 when self-priming)
Application temperatureair and substrate +10…+30 °C (recommended +10…+25 °C); material +15…+30 °C (recommended +17…+23 °C); air humidity no more than 80 %; substrate moisture no more than 5.0 % by weight; 3 °C above the dew point
Curinglight loads: +10 °C 32 h, +20 °C 16 h, +30 °C 12 h; foot traffic: 6 / 3 / 2 days; full strength gain: 10 / 7 / 5 days; next coat after 12–48 h at +20 °C; drying to degree 3 no more than 8 h
Key propertiesTaber abrasion resistance (CS10/1000 g/1000 rev.) no more than 65 mg; cross-cut adhesion no more than grade 1; gloss no more than 40 %; density of A+B 1.28–1.48 g/cm³; non-volatile content at least 94 %; anti-slip effect; bridges fine cracks; pot life +10 °C 60 min, +20 °C 30 min, +30 °C 15 min; service temperature from −10 to +60 °C
Consumption150–200 g/m² for 1 coat; 2 coats: 0.3–0.4 kg/m² (in the system, finishing layer in 2 passes 0.35 kg/m²); theoretical 1.41 kg/m² per 1 mm of coating
Shelf life6 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 20.30.12-069-94613022-2019; coating requirements per SP 71.13330.2017 cl. 8.12; test methods GOST 31992.1, GOST 31939, GOST 19007, GOST 31975, GOST 15140

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.