The polyurethane Floor 720 produces an elastic gloss coating: elongation at break at least 10%, tensile strength at least 35 MPa. The compound is two-component, low-viscosity, without a strong odour, with 100% non-volatiles. Intended for floors in medical and children’s facilities, offices, food, chemical and pharmaceutical production workshops, warehouses and car parks, including open ones. Service from −20 to +50 °C, resistance to water, petroleum products, salts, dilute acids and alkalis. It is poured over TAIKOR Primer 160.
| Manufacturer | TAIKOR (TECHNONICOL) — OOO “TECHNONICOL – Construction Systems” |
|---|---|
| Type | polyurethane floors |
| Use | production workshops, warehouses and logistics, car parks and ramps, food and pharmaceutical, retail and public, chemically resistant |
| Base | low-viscosity two-component polyurethane self-levelling compound without a strong odour; non-volatiles 100 % |
| Colour | tinted to any colour from the RAL catalogue; uniform gloss |
| Packaging | pails 5 and 20 l; net weight 4.8; 20.2 kg |
| Application method | over primed concrete/cement screed (TAIKOR Primer 160 primer recommended); substrate requirements as for Floor 710 (28 days, moisture no more than 4 wt. %, compressive strength at least 20 MPa, pull-off at least 1.5 MPa); A:B = 100:23.8 by weight; pour, gauge rake (for smooth coatings), roll with a spiked roller; working time on the floor about 30 min at +20 °C; addition/broadcasting of quartz sand is permitted |
| Application temperature | air +5…+25 °C, relative humidity no more than 80 %; substrate from +8 to +25 °C; surface 3 °C above the dew point |
| Curing | drying to degree 3 at +20 °C no more than 6 h; recoat window at least 24 h and no more than 72 h; full cure at least 7 days; of the TN-POL NALIVNOY PU system: walking after 36/24/18 h, light load 5/3/2 days, full 10/7/5 days at +10/+20/+30 °C |
| Key properties | Abrasion (CS10, 1000 cycles, ASTM D 4060) no more than 60 mg; tensile strength at least 35 MPa; elongation at break at least 10 %; Shore D hardness about 75; adhesion to concrete at least 2 MPa; service temperature -20…+50 °C; density 1.40-1.60 g/cm3; pot life at least 30 min; coating elasticity; resistance to water, petroleum products, salts, dilute alkalis and acids; in the TN-POL NALIVNOY PU system: RP1, V2, D2, T2, non-sparking — yes |
| Layer thickness | in the TN-POL NALIVNOY PU system 1.50-2.00 mm |
| Consumption | theoretical consumption at a 2 mm layer — 3 kg/m2; in the system 2.250-3.000 kg/m2 |
| Shelf life | 12 months; storage +5…+25 °C; transport -30…+30 °C |
| Standards | TU 20.30.22-144-72746455-2023; HS code (TN VED) 3214 90 0009 |
Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.
Deep-penetrating primer for dustproofing and hardening concrete floors and under TAIKOR Elastic 300 waterproofing; application from −10 °C.
One-component matt primer-enamel for economical painting of concrete floors with light and moderate loads, as well as metal; application from −30 °C.
Economical thin-layer floor based on TAIKOR Primer 150, quartz sand and Top 425 enamel for warehouses, car parks, stands and footpaths; UV-resistant.
Coloured thin-layer floor of TAIKOR Primer 150 primer-enamel and Top 425 enamel for production premises with dry and wet processes.
Antistatic polyurethane self-levelling floor for explosion-hazard production, electronics, laboratories, car services and filling stations; no more than 10⁶ Ω.
Epoxy primer without a strong odour for TAIKOR Floor self-levelling floors and a binder for repair compounds; adhesion to concrete from 2 MPa.