Elakor-PTs T4 Self-levelling Floor — thin-layer polyurethane-cement floor
ELAKOR

Elakor-PTs T4 Self-levelling Floor — thin-layer polyurethane-cement floor

Polyurethane-cement floors

The thin-layer version of the polyurethane-cement floor is spread with a squeegee rake with a notched blade and rolled with a spiked roller not later than 15 minutes after mixing. According to the technical data sheet, the coating performs indoors, under a canopy and outdoors and is designed for light and moderate intensity of mechanical exposure with heat and chemical resistance requirements. The substrate is concrete of at least M300; the compressive strength of the coating is 48 MPa, flexural strength 13 MPa, foot traffic after 24 hours.

Specifications

ManufacturerElakor — OOO “TEOKHIM-PROM”, Moscow Region
Typepolyurethane-cement floors
Useproduction workshops, warehouses and logistics, food and pharmaceutical, chemically resistant, outdoor areas
Basepolyurethane-cement three-component self-levelling compound (thin-layer self-levelling floor)
Colourgrey, light grey, beige, brown, yellow, blue, green, black; semi-matt/matt finish (the shade may change over time)
PackagingComp. “A” 9 kg + Comp. “B” 6.5 kg + Comp. “C” 14.5 kg = Kit 30 kg
Application methodSubstrate: monolithic concrete, concrete and sand-concrete screeds, grade strength not lower than M300 (B25), new concrete cured for at least 28 days; surface moisture is not limited (there must be no puddles); relative air humidity and dew point are not limited. Preparation: grinding with a terrazzo grinding machine (“000”/“00” segments) or shot blasting; primer Elakor-PTs Grunt (drying at least 24 h at +20°C). Mix only a full kit; spread with a squeegee rake with a notched blade, roll with a spiked roller (not later than 15 min).
Application temperatureair, surface: optimum +17…+23°C; permissible +10…+30°C; material temperature +18…+22°C
Curingpot life on the surface at (20±2)°C at least 15 min; at (20±2)°C, relative air humidity 70%: foot traffic – 24 h, full mechanical load – 7 days, full chemical load – 14 days
Key propertiesA:B:C ratio by weight 9 : 6.5 : 14.5; density 1.47±0.02 kg/l; adhesion (GOST 28574-2014) to concrete B25 > 2.5 MPa, to concrete B40 > 4.0 MPa (failure in concrete); compressive strength (28 days) 48 MPa; flexural 13 MPa; tensile 5 MPa; Shore D hardness at least 80-85; impact strength U-2M 100 cm; Taber abrasion CS-10, 1000 g, 14 days, not more than 20 mg; service temperature -30°C…+70°C continuous, short-term for up to 2 h up to 150°C; fire hazard class KM2 (V2, D1, T1, RP1); chemical resistance: water, salt and alkali solutions of any concentration, acid solutions up to 10-20%, oils and fats of all kinds, organic solvents, petrol, diesel fuel
Layer thickness1.5-2 mm
Consumptiontheoretical consumption 1.47 kg per 1 m² per 1 mm of layer; allowing for a 5% technological reserve – 1.55 kg
Shelf lifecomponents “A” and “B” – 12 months, component “C” – 6 months in the manufacturer's original packaging; store and transport at temperatures from +5° to +25°C

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.