LEVL Coat 310 — epoxy self-levelling floor, class KM1

Epoxy floors

LEVL Coat 310 self-levelling epoxy floor has fire hazard class KM1, confirmed by a certificate. The compound is laid over LEVL Coat 101/103 or 102W/106M primer, and in systems prior levelling with LEVL Self12 levelling compound over LEVL Base200 primer is mandatory. Taber abrasion is no more than 40 mg, Shore D hardness from 70, impact resistance high; the surface can be decorated with flakes and LEVL Coat 253 matt varnish. It is used in warehouses, workshops, covered car parks, schools, kindergartens, healthcare facilities, retail and exhibition halls.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Usewarehouses and logistics, production workshops, car parks and ramps, wet rooms, retail and public buildings, decorative, food and pharmaceutical, chemically resistant
Baseepoxy resin-based compound (two-component, coloured)
ColourRAL colours; gloss finish
Packagingmetal containers 25 kg (A+B); 2.4 kg (A+B); A : B = 4 : 1 (by weight)
Application methodself-levelling and highly filled coatings on cementitious substrates with high wear loads; in systems, levelling with LEVL Base200 + LEVL Self12 is mandatory; LEVL Coat 101/103 primer (up to 5 %) or 102W/106M (up to 10 %); squeegee with a B1/B2 notched blade (without sand: A2/A3); flakes and LEVL Coat 253 matt varnish optional; can be overcoated with a UV-resistant finish
Application temperatureambient and substrate +10…+30 °C; components and substrate optimally +15…+25 °C; air humidity no more than 80 %; substrate moisture no more than 5.0 % by weight (primer 101/103) or 10.0 % by weight (102W/106M); 3 °C above the dew point
Curinglight loads: +10 °C 32 h, +20 °C 16 h, +30 °C 12 h; foot traffic: 6 / 3 / 2 days; full loads: 10 / 7 / 5 days; next coat after 12–48 h at +20 °C
Key propertiesTaber abrasion resistance (CS10/1000 g/1000 rev.) no more than 40 mg; Shore D hardness (7 days) at least 70; adhesion (over LC 101 primer) at least 2.5 MPa (failure in the concrete); relative elongation at break at least 10 %; tensile strength at break at least 7 MPa; density 1.52 ± 0.05 g/cm³; non-volatile content at least 90 %; high impact resistance; pot life +10 °C 60 min, +20 °C 30 min, +30 °C 15 min; service temperature from −10 to +60 °C (highly filled: short-term up to +90 °C); fire hazard class KM1
Layer thicknessadmissible from 1 to 2 mm (incl. with sand); recommended 1.2 mm; highly filled from 3 to 12 mm
ConsumptionLEVL Coat 310: 1.5 kg/m² per 1 mm; with sand 1 : 0.5: 1.80 kg/m² per 1 mm; systems: smooth 1 mm — 1.5 kg/m² (or 1.2 kg/m² + sand 0.6 kg/m²), flakes 0.03 kg/m², LEVL Coat 253 matt varnish 0.08 kg/m² (options); textured 3.0 mm — main layer 1.1 kg/m² + sand 0.1–0.3 mm 0.5 kg/m² + 0.3–0.9 mm 4.0 kg/m² + finishing coat 0.9 kg/m²
Shelf life12 months from the date of manufacture; storage at +5…+30 °C
StandardsTU 2257-006-94613022-06 with Amendment No. 1; fire safety KM1 (RP1, V1, D1, T1), certificate RU C-RU.PB68.V.00646/21; substrate per SP 71.13330.2017 (cl. 8.12.2, Table 8.11); test methods GOST 31992.1, GOST 31939, GOST 28574, GOST 24621, GOST 11262

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.