LEVL Coat 318 — self-levelling epoxy floor
LEVL (INGRI)

LEVL Coat 318 — self-levelling epoxy floor

Epoxy floors

LEVL Coat 318 self-levelling epoxy compound gives a uniform gloss coating in RAL colours: smooth or textured, self-levelling or highly filled. It is laid over LEVL Coat 101, 102 W, 104 Rapid, 108 or 118 primers, with quartz sand added at 1 : 0.5 when filled. Shore D hardness is at least 75, Taber abrasion up to 60 mg, adhesion 2.5 MPa; the floor resists aggressive media and process water. It suits warehouses, assembly shops, garages, covered car parks, healthcare and educational institutions, pharmaceutical and chemical plants.

Specifications

ManufacturerLEVL (INGRI) — OOO “Ingri”, Saint Petersburg
Typeepoxy floors
Usewarehouses and logistics, production workshops, car parks and ramps, retail and public buildings, food and pharmaceutical, chemically resistant, wet rooms
Baseepoxy resin (two-component self-levelling compound)
ColourRAL colours; uniform gloss finish
Packagingkit of 2.4 and 30 kg; A : B = 7.4 : 1.0 (by weight)
Application methodself-levelling and highly filled, smooth and textured floor coatings over LEVL Coat 101 / 102 W / 103 / 104 Rapid / 108 / 118 primer: pouring, squeegee or notched trowel, rolling with a spiked roller; filling with sand 1 : 0.5; before varnishing, wait at least 3 days or clean with LEVL FloorAntisept 831
Application temperatureair and substrate +10…+30 °C (recommended +17…+23 °C); material +15…+25 °C; air humidity no more than 80 %; substrate moisture no more than 5 % (primers 101/103/104 Rapid/108/118) or 10 % (102 W); 3 °C above the dew point
Curinglight loads / recoat interval: +10 °C ~32 h, +20 °C ~16 h, +30 °C ~12 h; foot traffic ~6 / ~3 / ~2 days; full strength gain ~10 / ~7 / ~5 days
Key propertiesShore D hardness (7 days) at least 75; Taber abrasion (CS10 / 1000 g / 1000 rev.) no more than 60 mg; adhesion (with LEVL Coat 101 primer) at least 2.5 MPa (failure in the concrete); tensile strength at break at least 8 MPa; relative elongation at least 2 %; density 1.65 ± 0.05 g/cm³; non-volatile content at least 97 %; pot life +10 °C 60 min, +20 °C 30 min, +30 °C 15 min; service temperature from −10 to +60 °C (highly filled: short-term up to +90 °C); chemical resistance: on request
Layer thicknessfrom 1.5 to 5.0 mm (recommended 2.0 mm); unfilled 1.5–4.0 mm
Consumptionsmooth 2 mm: 3.3 kg/m²; smooth filled 1 : 0.5, 2 mm: 2.5 kg/m² + quartz sand 0.1–0.3 mm 1.25 kg/m²; theoretically per 1 mm: unfilled 1.65 kg/m², with sand 1.0 : 0.5 — 1.88 kg/m²
Shelf life12 months from the date of manufacture; storage at +5…+25 °C
StandardsTU 2257-006-94613022-2006; works per SP 29.13330.2011 and SP 71.13330.2017 (Table 8.12); test methods GOST 31992.1, GOST R 31939, GOST 24621, GOST 11262, GOST 28574

Data from the manufacturer’s technical data sheet. The coating system, number of coats and quantity are selected for your project on request.